K. T. Park, J. H. Park, Y. S. Lee and W. J. Nam, “Microstructures Developed by Compressive Deformation of Coarse Grained and Ultrafine Grained 5083 Al Alloys at 77 K and 298 K,” Materials Science and Engineering: A, Vol. 408, 2005, pp. 102-109. doi:10.1016/j.msea.2005.07.040

has been cited by the following article:

• TITLE: Effect of Hot Accumulative Roll Bonding Process on the Mechanical Properties of AA5083

  AUTHORS: Hassan Sheikh, Ebrahim Paimozd

  KEYWORDS: Grain refinement; Aaccumulative Roll Bonding; Mechanical Characterization; Aluminum Alloys

  JOURNAL NAME: Open Journal of Metal, Vol.1 No.1, September 28, 2011

  ABSTRACT: In this work, accumulative roll bonding (ARB) process as a severe plastic deformation was applied on an AA5083 sheet up to 6 cycles at the temperature of 300℃ and at the strain rate of 50 s­‐1. The results of tensile tests show that the values of the yield stress and the ultimate tensile strength don't change considerably after 4 cycles. Also, transmission electron microscopy (TEM) micrograph confirmed that the microstructure has fine (sub) grains with the size of 200 nm - 400 nm.