High Temperature Oxidation and Hot Corrosion Behaviour of Yttria- Stabilised Zirconia as Plasma Sprayed Coating in Air and Salt at 900°C under Cyclic Condition
AUTHORS:
Dinesh Gond, R.S. Lalbondre, D. Puri, S. Prakash
KEYWORDS:
Hot corrosion; T-91; Plasma spray coating.
JOURNAL NAME:
Journal of Minerals and Materials Characterization and Engineering,
Vol.11 No.3,
March
20,
2012
ABSTRACT: Yttria-Stabilised Zirconia (YSZ) coatings were deposited on a T-91 boiler steel. NiCrAlY was used as bond coat and YSZ as top coat. Hot corrosion studies were conducted on uncoated as well as plasma spray coated specimens in air as well as salt (75wt. % Na2SO4 + 25wt. % NaCl) at 900°C under cyclic conditions. The thermogravimetric technique was used to establish kinetics of corrosion. X-ray diffraction (XRD) and scanning electron microscopy/energy-dispersive x-ray analysis (SEM/EDAX) techniques were used to analyse the corrosion products. This YSZ overlay coatings enhance resistance to corrosion significantly which can be attributed to formation of zirconium oxides (ZrO2) and yttrium oxide (Y2O3). This coating was more effective in salt environment and there is an extra phase of ZrS.