R. K. Islamgaliev, N. F. Yunusova, R. Z. Valiev, N. K. Tsenev, V. N. Perevezent-sev and T. G. Langdon, “Characteristics of Superplasticity in an Ultrafine-Grained Aluminum Alloy Processed by ECA Pressing,” Scripta Materialia, Vol. 49, 2003, pp. 467-472. doi:10.1016/S1359-6462(03)00291-4

has been cited by the following article:

• TITLE: Effect of Hot Accumulative Roll Bonding Process on the Mechanical Properties of AA5083

  AUTHORS: Hassan Sheikh, Ebrahim Paimozd

  KEYWORDS: Grain refinement; Aaccumulative Roll Bonding; Mechanical Characterization; Aluminum Alloys

  JOURNAL NAME: Open Journal of Metal, Vol.1 No.1, September 28, 2011

  ABSTRACT: In this work, accumulative roll bonding (ARB) process as a severe plastic deformation was applied on an AA5083 sheet up to 6 cycles at the temperature of 300℃ and at the strain rate of 50 s­‐1. The results of tensile tests show that the values of the yield stress and the ultimate tensile strength don't change considerably after 4 cycles. Also, transmission electron microscopy (TEM) micrograph confirmed that the microstructure has fine (sub) grains with the size of 200 nm - 400 nm.