J. M. Torralba, F. Velasco, C. E. DA Costa, I. Vergara and D. Caceres, “Mechanical Behaviour of the Interphase between Matrix and Reinforcement of Al 2014 Matrix Composites Reinforced with (Ni3Al)p,” Composites Part A, Vol. 33, No. 3, 2002, pp. 427-434.

has been cited by the following article:

• TITLE: Evaluation of Characteristics of Interfacial Phases Produced in Al/Ni3Al Composite during Manufacturing

  AUTHORS: Seyed Abdolkarim Sajjadi, Maryam Abbasi, Mazyar Azadbeh

  KEYWORDS: Metal-Matrix Composites (MMCs), Interface, X-Ray Diffraction (XRD), Powder Processing

  JOURNAL NAME: Materials Sciences and Applications, Vol.2 No.9, September 20, 2011

  ABSTRACT: Metal matrix composites (MMCs) are currently being investigated because of their superior properties. The properties are mainly attributed to the efficiency of the load transfer from the matrix to the reinforcements through the matrix-reinforcement interface. The aim of this study is to investigate the effect of manufacturing parameters on the microstructure and morphology of the interface and the aluminide phases formed at the matrix-reinforcement interfaces. The parameters are: milling time to fabricate Ni3Al, method of mixing of Ni3Al and Al powders, compaction pressure and sintering temperature. The composite studied in this research was Al/5 Vol% Ni3Al made from two different types of Ni3Al powders. The results showed that compacting and sintering at higher levels lead to the transformation of Ni3Al particles to thin layers of Al3Ni. It was also shown that the prolonged milling time to produceNi3Alreinforcements and the prolonged ball milling procedure for mixing the powders, both, promote the diffusion process at reinforcement/matrix interface.