V. F. Dorfman, “Diamond-like nanocomposites (DLN),” Thin Solid Films, Vol. 212, No. 1-2, 1992, pp. 267-273.
http://dx.doi.org/10.1016/0040-6090(92)90532-G

has been cited by the following article:

  • TITLE: Improvement of Thermal Stability and Tribological Performance of Diamond-Like Carbon Composite Thin Films

    AUTHORS: Chavin Jongwannasiri, Xianghui Li, Shuichi Watanabe

    KEYWORDS: Diamond-Like Carbon; Thermal Stability; Tribological Performance

    JOURNAL NAME: Materials Sciences and Applications, Vol.4 No.10, October 17, 2013

    ABSTRACT: Diamond-like carbon (DLC) is a metastable amorphous film that exhibits unique properties. However, many limitations exist regarding the use of DLC, for example, its tribological characteristics at high temperature, as well as its limited thermal stability. In this study, silicon/oxygen and silicon/nitrogen co-incorporated diamond-like carbon (Si-O-DLC and Si-N-DLC) films are studied, taking into account the thermal stability and tribological performance of these films compared with pure DLC. All the films were prepared on Si wafers, WC-Co materials, and aluminum foils using a plasma-based ion implantation (PBII) technique using acetylene (C2H2), tetramethylsilane (TMS, Si(CH3)4), oxygen (O2) and nitrogen (N2) as plasma sources. The structure of the films was characterized using Raman spectroscopy. The thermal stability of the films was measured using thermogravimetric and differential thermal analysis (TG-DTA). The friction coefficient of the films was assessed using ball-on-disk friction testing. The results indicate that Si-N-DLC films present better thermal stability due to the presence of Si-O networks in the films. The Si-N-DLC (23 at.%Si, 8 at.%N) film was affected using thermal annealing in an air atmosphere with increasing temperature until 500°C. The film can also resist thermal shock by cycling 10 times between the various temperatures and air atmosphere until 500°C. Further, Si-O-DLC and Si-N-DLC films exhibit excellent tribological performance, especially the Si-N-DLC (23 at.%Si, 8 at.%N) film, which exhibits excellent tribological performance at 500°C in an air atmosphere. It is concluded that Si-O-DLC and Si-N-DLC films improve upon the thermal stability and tribological performance of DLC.