Y. Chen, et al., “Layer-by-Layer Growth of ZnO Epilayer on Al2O3(0001) by Using a MgO Buffer Layer,” Applied Physics Letters, Vol. 76, No. 5, 2000, pp. 559-561. doi:10.1063/1.125817

has been cited by the following article:

• TITLE: ZnO Heteroepitaxy on Sapphire Using a Novel Buffer Layer of Titanium Oxide: Crystallographic Behavior

  AUTHORS: Satoshi Yamauchi, Yoh Imai

  KEYWORDS: ZnO; Ti2O3; Plasma-Assisted Epitaxy; Hexagonal Pyramid Grain

  JOURNAL NAME: Crystal Structure Theory and Applications, Vol.2 No.2, June 14, 2013

  ABSTRACT: A novel buffer layer consists of titanium oxide grown on a-sapphire by low-pressure chemical vapor deposition using titanum-tetra-iso-propoxide and oxygen gas was used for ZnO epitaxial growth at temperature as low as 340℃ by plasma-assisted epitaxy using radio-frequency oxygen-gas plasma. XRD and RHEED indicated (0001)Ti2O3 layer in corundum crystal system was epitaxially grown on the substrate in an in-plane relationship of [1-100]Ti2O3// [0001]Al2O3 by uniaxial phase-lock system. Growth behavior of ZnO layer was significantly dependent on the Ti2O3 buffer-layer thickness, for example, dense columnar ZnO-grains were grown on the buffer layer thinner than 10 nm but the hexagonal pyramid-like grains were formed on the thin buffer layers below 2 nm. RHEED observations showed ZnO layer including the pyramid-like grains was epitaxially grown with single-domain on the thin buffer layer of 0.8 nm in the in-plane relationship of [1-100]ZnO//[1-100]Ti2O3//[0001]Al2O3, whereas the multi-domain was included in ZnO layer on the buffer layer above 10 nm.