Prevosto, D., Capaccioli, S., Sharifi, S., Kessairi, K. Lucchesi, M. and Rolla, P.A. (2007) Secondary dynamics in glass formers: Relation with the structural dynamics and the glass transition. Journal of Non-Crystalline Solids, 353, 4278-4282. doi:10.1016/j.jnoncrysol.2007.03.045

has been cited by the following article:

• TITLE: Ratio of dielectric strength of structural and secondary relaxation close to the glass transition for PPGE and DGEBA

  AUTHORS: Soheil Sharifi, Nima bahreini

  KEYWORDS: Dielectric Strength; Glass Transition; PPGE; DGEBA; Pressure and Temperature

  JOURNAL NAME: Natural Science, Vol.4 No.7, July 10, 2012

  ABSTRACT: Here, dielectric spectroscopy is used in the fre- quency range from 10-2 Hz up to 107 Hz and we found dynamics of the primary α-and intermolecular Johari–Goldstein β-processes are strongly correlated in diglycidyl-ether of bis-phenol-A and poly phenyl glycidyl-ether (PPGE) over a wide temperature from 193 to 345 K and pressure P range from 0.1 to 600 MPa. In contrast with the widespread opinion of statistical independence of these processes the α-β mutual dependence is quantitatively confirmed in [1] analysing the temperature and pressure behavior of the α-and (JG) β-processes the investigation of the ratio of dielectric strength of two processes close to Tg evidence that the importance of secondary dy namics in relaxing external electric stresses increase in glass formers at high pressures with respect to that of the structural relaxation. We suggest that the thermal agitation, acting above Tg is at the basis of the observed result.