B. Wilshire and C. J. Palmer, “Strain Accumulation during Dislocation Creep of Prestrained Copper,” Materials Science and Engineering: A, Vol. 387-389, 2004, pp. 716- 718.

has been cited by the following article:

• TITLE: Localization of Plastic Deformation in Copper Canisters for Spent Nuclear Fuel

  AUTHORS: Kati Savolainen, Tapio Saukkonen, Hannu Hänninen

  KEYWORDS: Copper; Deformation; Localization; Friction stir Welding; Electron Beam Welding

  JOURNAL NAME: World Journal of Nuclear Science and Technology, Vol.2 No.1, December 31, 2011

  ABSTRACT: Localization of plastic deformation in different parts (extruded and forged base materials as well as EB and FSW welds) of the corrosion barrier copper canister for final disposal of spent nuclear fuel was studied using tensile testing, optical strain measurement, scanning electron microscopy (SEM), and electron back-scatter diffraction (EBSD). Results show that in the base materials plastic deformation occurs very uniformly. In FSW welds the deformation localizes in the weld either at the processing line or at a line of entrapped oxide particles. In EB welds the deformation localizes to the equally oriented large grains at the weld centreline or at the steep grain size gradient in the fusion line.