Z. He, C. Zhong , X. Huang , W. Y. Wong, H. Wu, L. Chen, S. Su and Y. Cao, “Simultaneous Enhancement of Open-Circuit Voltage, Short-Circuit Current Density, and Fill Factor in Polymer Solar Cells,” Advanced Materials, Vol. 23, No. 40, 2011, pp. 4636-4643. doi:10.1002/adma.201103006

has been cited by the following article:

• TITLE: Effect of PEDOT:PSS Layer and ITO Ozonization in Arylenevinylene-co-Pyrrolenevinylene (AVPV) Based Solar Cell Devices

  AUTHORS: Ankur Solanki, S. Sundar Kumar Iyer, Ashish Garg

  KEYWORDS: AVPV, Organic Polymers, Ozonization, PEDOT:PSS, Organic Solar Cells

  JOURNAL NAME: Materials Sciences and Applications, Vol.2 No.12, December 22, 2011

  ABSTRACT: Arylenevinylene-co-pyrrolenevinylene (AVPV) is polymer oligomer system derived from arylbridged bispyrroles which has been explored for photovoltaic devices. In this paper, we show the dependence of the photovoltaic device parameters on the anode surface treatment in an organic single layer photovoltaic device based on AVPV as an electron donor. Since the total quantum efficiency includes the charge collection efficiency at the electrodes, experiments were carried out to vary the anode (ITO) characteristics, achieved by using ITO with or without ozonization and with or without PEDOT:PSS (Polyethylene dioxythiophene:Polystyrene sulphonic acid) layer. Devices fabricated on ITO anode (without ozonization and without PEDOT:PSS) exhibited the maximum current density (Jsc = 1.3 µA·cm–2) as compared to those devices where ITO was ozonized as well as had a PEDOT:PSS layer (Jsc = 0.1 µA·cm–2) measured under 1 sun illumination of AM 1.5 through a calibrated solar simulator.