Muñoz-Cubillos, J., Coronado, J.J. and Rodríguez, S.A. (2017) Deep Rolling Effect on Fatigue Behavior of Austenitic Stainless Steels. International Journal of Fatigue, 95, 120-131.
https://doi.org/10.1016/j.ijfatigue.2016.10.008

has been cited by the following article:

• TITLE: Fatigue Response of Cold-Rolled Type-304 Stainless Steel Foil

  AUTHORS: Thomas P. Kieffer, James I. Hardy

  KEYWORDS: Fatigue, Cold-Rolled Foil, Type-304 Stainless Steel, Resistive-Sensing, Anisotropy

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.9 No.1, January 29, 2021

  ABSTRACT: This study presents the fatigue response of 304 stainless steel foil, cold-rolled to a thickness of 3.2 μm with 87 percent cold work at orientations of 0, 45, and 90 degrees to the direction of rolling. Fatigue specimens were fabricated by laminating a supportive layer of 20-μm polyimide film to one side of the foil and patterning 242 crack initiation features by photolithographic process. Progression of fatigue damage was determined through electrical resistance measurement. The fatigue response was demonstrated to be largely affected by anisotropy existing between the rolling direction and the off-axis orientations. Fatigue cracks that traveled in a direction parallel to the elongated grains (cyclic loads applied at 90-degree orientation to foil rolling direction) had the most fatigue response (undesirable characteristic). The construction of the specimens with thin foil supported by a film backing contributed to high fatigue threshold.