Ouajai, S. and Shanks, R.A. (2009) Composition, Structure and Thermal Degradation of Hemp Cellulose after Chemical Treatments. Polymer Degradation and Stability, 89, 327-335.
https://doi.org/10.1016/j.polymdegradstab.2005.01.016

has been cited by the following article:

• TITLE: Characterization of Peanut Shells for Their Valorization in Earth Brick

  AUTHORS: Ouanmini Bobet, Sory Nassio, Mohamed Seynou, Bakiono Remy, Lamine Zerbo, Issiaka Sanou, Moustapha Sawadogo, Younoussa Millogo, Escadeillas Gilles

  KEYWORDS: Agricultural Wastes, Peanut Shells, Thermal Conductivity, Adobes, Durability

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.8 No.4, July 30, 2020

  ABSTRACT: Peanut shells from Burkina Faso were characterized using mineralogical, microstructural and chemical methods to perform its possibility to be used as reinforce in adobe bricks. It consists of cellulose (48 wt%), hemicellulose (3 wt%) and lignin (28 wt%). The peanut shells were characterized by high porosity and showed water absorption around 198% at 72 hours. Its chemical composition is essentially composed of silica, iron oxides, alumina and calcium oxide. Its microstructure showed that the peanut shells were a compilation of microfibers with high porous of borders. In watery solution, the peanut shells released polyphenols. Thermal conductivity of peanut at 25 °C was 0.155 ± 0.021 W/mK. The physico-chemical characteristics of peanut shells were similar to those found with agricultural by-products used in adobe reinforce.