Song, R.G. and Zhang, Q.Z. (2001) Heat Treatment Optimization for 7175 Aluminum Alloy by Genetic Algorithm. Materials Science and Engineering: C, 17, 133-137.
https://doi.org/10.1016/S0928-4931(01)00321-6

has been cited by the following article:

• TITLE: Effect of Pre-Aging, Over-Aging and Re-Aging on Exfoliation Corrosion and Electrochemical Corrosion Behavior of Al-Zn-Mg-Cu Alloys

  AUTHORS: Xingzhi Liao, Xiaohua Kong, Pengxuan Dong, Kanghua Chen

  KEYWORDS: Al-Zn-Mg-Cu-Zr Alloys, Pre-Aging, Over-Aging and Re-Aging, Exfoliation Corrosion, Electrochemical Corrosion

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.8 No.2, February 26, 2020

  ABSTRACT: By means of TEM, hardness, conductivity, tensile strength test, fracture toughness test, polarization curve and EIS, the Al-Zn-Mg-Cu alloys treated by a new multi-stage aging system, i.e. pre-aging, over-aging and re-aging (120°C/24h + 160°C/8h + 120°C/24h), were characterized. It is found that compared with the Al-Zn-Mg-Cu alloys treated by T76 (120°C/24h + 160°C/8h), the new multi-stage aging treatment can improve the tensile strength, fracture toughness, hardness and conductivity of the alloys at the same time. This is mainly due to the pre-aging, over-aging and re-aging process of super high strength aluminum alloys. Compared with the two-stage over aging process, the formation of multi-stage multi-phase precipitation structure can improve the strength, toughness and corrosion resistance of the alloys at the same time. The polarization curve is consistent with the conclusion. Therefore, we conducted this study to test how the comprehensive properties of the alloy can be improved.