La2O3/Fe2O3-CeO2 Composite Oxide Catalyst and Its Performance
AUTHORS:
Youfeng Li, Jinliang Lin, Guangwei Wang
KEYWORDS:
La2O3/Fe2O3-CeO2, Composite Oxide, Synthetic Method, Catalytic Degradation, Wastewater Treatment
JOURNAL NAME:
Advances in Materials Physics and Chemistry,
Vol.9 No.12,
December
11,
2019
ABSTRACT:
The La2O3/Fe2O3-CeO2 composite oxide catalysts were prepared by coprecipitation method, sol-gel method
and hydrothermal method. The effect of preparation methods on structure morphology
and photocatalytic properties of La2O3/Fe2O3-CeO2 samples was investigated. The results show that the cubic CeO2 structure
can be obtained at 600℃. The rod-shaped sample prepared by coprecipitation method,
displays the highest crystalline and the strongest diffraction peak intensity. The
spherical sample is acquired from sol-gel method, while the small granular sample
prepared by hydrothermal method tends to aggregate. The maximum specific surface
area of the sample prepared by coprecipitation method is 76.21 m2/g,
the minimum specific area of the sample from sol-gel method is 32.66 m2/g
and the maximum pore size is 13.84 nm, while the minimum pore volume and pore size
of the sample by hydrothermal method are 0.038 cm3/g and 3.95 nm respectively.
The band gap energy of catalyst samples is in the following order: sample-CP (c0/ct) = kt + qe. The maximum k-value of the sample degradation process obtained by coprecipitation method
is 0.074 min-1.
Related Articles:
Retraction：Erratum to “Intercalation of Amines into Layered Calcium Phosphate and Their New Behavior for Copper Retention from Ethanolic Solution” [Open Journal of Synthesis Theory and Applications 2 (2013) 1-7]
Camila F. N. da Silva, Ana Paula B. Dias, Ana Paula R. Santana, Jéssica S. Pizzo, Fernando M. de Souza, Angélica M. Lazarin, Rosana L. Sernaglia, Elza I. S. Andreotti
DOI:
10.4236/ojsta.2015.41002
4,957 Downloads 5,632 Views Citations
Pub. Date:
January
12,
2015