Bentz, D.P., Ardani, A., Barrett, T., Jones, S.Z., Lootens, D., Peltz, M.A., et al. (2015) Multi-Scale Investigation of the Performance of Limestone in Concrete. Construction and Building Materials, 75, 1-10.
https://doi.org/10.1016/j.conbuildmat.2014.10.042

has been cited by the following article:

• TITLE: Effect of Additional Surfaces on Ordinary Portland Cement Early-Age Hydration

  AUTHORS: Tapio Vehmas, Anna Kronlöf, Andrzej Cwirzen

  KEYWORDS: Ordinary Portland Cement, Hydration, Early-Age, Surfaces, Autocatalytic Reaction

  JOURNAL NAME: Materials Sciences and Applications, Vol.8 No.12, November 10, 2017

  ABSTRACT: Early-age hydration of Ordinary Portland Cement (OPC) was studied in the presence of two additional surfaces. Additional surfaces are known to accelerate the early-age hydration of OPC. Autocatalytic reaction modelling was used to determine acceleration mechanism of additional surfaces. Heat development of the hydration was measured with semi-adiabatic calorimetry and the results were modelled with an autocatalytic reaction. Autocatalytic reaction modelling was able to determine number of initially active nucleation sites in early-age hydration. OPC hydration followed autocatalytic reaction principles throughout induction period and accelerating period. Both of the added surfaces, limestone filler and calcium-silicate-hydrate (C-S-H) coated limestone filler accelerated the early-age hydration. According to autocatalytic modelling, the C-S-H coated filler increased the number of initially active nucleation sites. Pristine limestone filler accelerated the early-age hydration by providing the additional nucleation sites throughout the early-age hydration. The difference was explained with common theories of nucleation and crystal growth. Autocatalytic model and measured calorimeter curve started to significantly deviate at the inflection point, where the reaction mode changed. The reaction mode change depended on the average particle distance. Early-age hydration, modelled as autocatalytic reaction was able to improve understanding of OPC early-age hydration and quantify the number of initially active nucleation sites. Understanding and quantifying the acceleration mechanisms in early-age hydration will aid larger utilization of supplementary cementitious materials where understanding the early-age strength development is crucial.