Saitou, N., Enomoto, K., Kurosawa, K., Morinaka, R., Hayashi, E., Ishikawa, T. and Yoshimura, T. (2003) Development of Water Jet Peening Technique for Reactor Internal Components of Nuclear Power Plant. Journal of Jet Flow Engineering, 20, 4-12.

has been cited by the following article:

• TITLE: Evolution of Microstructure from the Surface to the Interior of Cr-Mo Steel by Water Jet Peening

  AUTHORS: Masataka Ijiri, Daichi Shimonishi, Daisuke Nakagawa, Toshihiko Yoshimura

  KEYWORDS: Water Jet Peening, Cr-Mo Steel, Surface Reforming, Microstructure, Voids

  JOURNAL NAME: Materials Sciences and Applications, Vol.8 No.10, September 7, 2017

  ABSTRACT: The microstructure and hardness on and below the surface of Cr-Mo steel (SCM435) treated by water jet peening (WJP) were investigated using scanning electron microscopy and micro Vickers hardness measurements. The change of the surface residual stress caused by the WJP treatment influenced the surface microstructure and surface hardness of the SCM435 steel. Cementite in the pearlite phase tended to protrude as the duration of WJP was increased. Voids were formed in the area 0.5 - 1.0 mm below the surface and also at grain boundaries between ferrite and pearlite grains, whereas no voids were formed in the depth range from 2.0 to 3.0 mm below the surface.