G. J. Redhammer, G. Tippelt, G. Roth and G. Amthauer, “Structural Variations in the Brownmillerite Series Ca2(Fe2–xAlx)O5: Single-Crystal X-Ray Diffraction at 25±?C and High-Temperature X-Ray Powder Diffraction (25±?C ? T ? 1000±?C),” American Mineralogist, Vol. 89, 2004, pp. 405-420.

has been cited by the following article:

• TITLE: Temperature Dependence of the Magnetic and Electric Properties of Ca2Fe2O5

  AUTHORS: Cléber Candido da Silva, Antonio S. B. Sombra

  KEYWORDS: Ca2Fe2O5, Dielectric Measurements, Magnetization

  JOURNAL NAME: Materials Sciences and Applications, Vol.2 No.9, September 20, 2011

  ABSTRACT: Ca2Fe2O5 powder sample, were prepared to investigate the origin of the weak ferromagnetic component reported in literature for calcium ferrite single crystals. In this work, the calcination method was used to produce nanocrystalline powders of Ca2Fe2O5. XRD measurement has shown the presence of Fe3O4 magnetite and CaO as impurity phases. The ferrimagnetic phase deeply influences the magnetic behavior with features very similar to those reported in literature for Ca2Fe2O5, both powders and single crystals. Our results support the hypothesis that the weak ferromagnetic component observed in Ca2Fe2O5 can be also due to the presence of magnetite impurity traces in the samples. The powders were submitted to calcination processes at 500℃ for 2 hours and 950℃ for 16 hours. The sintered sample was submitted at 1050℃ for 6 hours and characterized by X-Ray Powder diffraction (XRD), dielectric measurements, Magnetization and Scanning Electron Microscopy (SEM) analysis.