Liu, X.F., Zhu, Y.F. and Li, L.Q. (2008) Structure and hydrogenation properties of nanocrystalline Mg2Ni pre-pared by hydriding combustion synthesis and mechanical milling [J]. Journal of Alloys Compounds, 455, 197-202.

has been cited by the following article:

• TITLE: Hydriding and dehydriding kinetics of melt spun nanocrystalline Mg20Ni10-xCux (x = 0-4) alloys

  AUTHORS: Yang-Huan Zhang, Dong-Liang Zhao, Bao-Wei Li, Hui-Ping Ren, Shi-Hai Guo, Xin-Lin Wang

  KEYWORDS: Mg2Ni-Type Alloy; Substituting Ni with Cu; Melt Spinning; Hydriding and Dehydriding

  JOURNAL NAME: Natural Science, Vol.2 No.1, January 28, 2010

  ABSTRACT: The nanocrystalline Mg2Ni-type electrode alloys with nominal compositions of Mg20Ni10-xCux (x = 0, 1, 2, 3, 4) were synthesized by melt-spinning technique. The microstructures of the alloys were characterized by XRD, SEM and HRTEM. The hydrogen absorption and desorption kinet-ics of the alloys were measured using an auto-matically controlled Sieverts apparatus. The re- sults show that all the as-spun alloys hold ty- pical nanocrystalline structure. The substitution of Cu for Ni does not change the major phase Mg2Ni but it leads to the formation of the sec-ondary phase Mg2Cu. The hydrogen absorption capacity of the alloys first increases and then decreases with rising Cu content, but the hy-drogen desorption capacity of the alloys mono- tonously grows with increasing Cu content. The melt spinning significantly improves the hydro- genation and dehydrogenation capacities and kinetics of the alloys.