Article citations


Abdelal, N. (2013) Effect of Voids on Delamination Behavior under Static and Fatigue Mode I and II. Ph.D. Dissertation, University of Dayton, Dayton.

has been cited by the following article:

  • TITLE: Porosity Effects on Interlaminar Fracture Behavior in Carbon Fiber-Reinforced Polymer Composites

    AUTHORS: Issa A. Hakim, Steven L. Donaldson, Norbert G. Meyendorf, Charles E. Browning

    KEYWORDS: Carbon Fiber Reinforced Composite, Nondestructive Evaluation, Porosity, Fatigue Fracture Behavior, Serial Sectioning

    JOURNAL NAME: Materials Sciences and Applications, Vol.8 No.2, February 6, 2017

    ABSTRACT: Fiber-reinforced polymer composite materials have become materials of choice for manufacturing application due to their high specific stiffness, strength and fatigue life, low density and thermal expansion coefficient. However, there are some types of defects such as porosity that form during the manufacturing processes of composites and alter their mechanical behavior and material properties. In his study, hand lay-up was conducted to fabricate samples of carbon fiber-reinforced polymer composites with three different vacuum levels in order to vary porosity content. Nondestructive evaluation, destructive techniques and mechanical testing were conducted. Nondestructive evaluation results showed the trend in percentages of porosity through-thickness. Serial sectioning images revealed significant details about the composite’s internal structure such as the volume, morphology and distribution of porosity. Mechanical testing results showed that porosity led to a decrease in both Mode I static interlaminar fracture toughness and Mode I cyclic strain energy release rate fatigue life. The fractographic micrographs showed that porosity content increased as the vacuum decreased, and it drew a relationship between fracture mechanisms and mechanical properties of the composite under different modes of loading as a result of the porosity effects. Finally, in order to accurately quantify porosity percentages included in the samples of different vacuum levels, a comparison was made between the parameters and percentages resulted from the nondestructive evaluation and mechanical testing and the features resulted from fractography and serial sectioning.