Kovacs, B.V. (1994) Alloying Elements and Heat Treatment of ADI. 2nd International ADI Seminar, Helsinki University of Technology, 1-3 June 1994, 1-12.

has been cited by the following article:

• TITLE: Microstructure, Mechanical Properties, Toughness, Wear Characteristics and Fracture Phenomena of Austenitised and Austempered Low-Alloyed Ductile Iron

  AUTHORS: Nabil Fatahalla, Osama Hussein

  KEYWORDS: Austempered Ductile Iron, Low-Alloyed Ductile Iron, Tensile Properties, Wear Characteristics, Microstructure, Hardness

  JOURNAL NAME: Open Access Library Journal, Vol.2 No.1, January 30, 2015

  ABSTRACT: Conventional ductile iron (DI) and austempered ductile iron (ADI) alloys were successfully produced. The alloying elements—Ni, Mo, Cr and Mn were added to get as-cast low-alloyed ductile iron (LADI) followed by austempering heat treatment. Hardness was measured for all investigated alloys. A hardness conversion table was deduced for irons investigated. Highest values of calculated quality index (QI) were for ADI alloys implying higher material performance. Impact energy values were attributed to microstructure and tensile properties. Wear characteristics of selected ADI alloys showed comparable values with LADI. Micro-hardness values were used to identify the micro-constituents and the work-hardened layers. Fracture modes were revealed and fracture surface observations were done by SEM. Due to higher toughness and QI, and cheap price, it is suggested that rolling mills may be produced from ADI, specially heat-treated instead of LADI.