Sha, G. and Cerezo, A. (2004) Early-Stage Precipitation in Al-Zn-Mg-Cu Alloy (7050). Acta Materialia, 52, 4503- 4516.
http://dx.doi.org/10.1016/j.actamat.2004.06.025

has been cited by the following article:

• TITLE: Effect of Retrogression and Reaging on Stress Corrosion Cracking of Spray Formed Al Alloy

  AUTHORS: Ruiming Su, Yingdong Qu, Xiang Li, Junhua You, Rongde Li

  KEYWORDS: Spray Forming, Al-Zn-Mg-Cu Alloy, Retrogression and Reaging, Stress Corrosion Cracking

  JOURNAL NAME: Materials Sciences and Applications, Vol.7 No.1, January 28, 2016

  ABSTRACT: Stress corrosion cracking (SCC) resistance of a spray formed Al-Zn-Mg-Cu alloy underwent retrogression and reaging (RRA) was studied by slow strain rate tests in dry air and 3.5 wt% NaCl solution. The results showed that after RRA treatment, interrupted η phases at grain boundaries and slightly wide precipitate free zones could decrease SCC susceptibility of the alloy. Lots of reticular dislocations appeared in deformation process could prevent hydrogen induced cracking, and then SCC. Abundance transgranular dispersive η' phases separated out again promoted tensile strength to 759.4 MPa. The fracture ways of the specimens were dimple fracture in dry air and sub-cleavage fracture in 3.5% NaCl solution.