Toutanji, H., Delatte, N., Aggoun, S., Duval, R.and Danson, A. (2004) Effect of Supplementary Cementitious Materials on the Compressive Strength and Durability of Short-Term Cured Concrete. Cement and Concrete Research, 34, 311-319.
http://dx.doi.org/10.1016/j.cemconres.2003.08.017

has been cited by the following article:

• TITLE: Influence of Nano-Barium Sulfate Agglomeration on Microstructure and Properties of the Hardened Cement-Based Materials

  AUTHORS: Mohamed El-Shahate Ismaiel Saraya, Inas Mostafa Bakr

  KEYWORDS: Nano-Barium Sulfate, Cement Paste, Filler, Compressive Strength, Microstructure

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.3 No.11, November 27, 2015

  ABSTRACT: The aim of the present work is to study the effect of Nano-barium sulfate additions on the physic-mechanical properties of hardened cement pastes. Nano-barium sulfate was prepared by the precipitation method. Eight mixes of filled cement pastes containing 0.5 wt%, 1.0 wt%, 1.5 wt% and 2.0 wt% of both nano-barium sulfate and micro-limestone were prepared and compared to the base OPC. The hydration characteristics were evaluated by the measure of combined water content, bulk density, total porosity and compressive strength for samples hydrated up to 90 days. The progress of hydration reactions was followed up by XRD analysis. The morphology and microstructure were studied by SEM. Nano-size barium sulfate acted as a nucleating agent and enhanced the hydration of cement pastes up to 2.0% mass content. Also, the microstructure was improved considerably. Accordingly, nano-size barium sulfate can be used successfully in the preparation of filled cement.