Jeon, H., Kim, D.J. and Kim, J.H. (2014) Synthesis of Mesoporous MgO Catalyst Templated by a PDMS-PEO Comb-Like Copolymer for Biodiesel Production. Fuel Processing Technology, 116, 325-331.
http://dx.doi.org/10.1016/j.fuproc.2013.07.013

has been cited by the following article:

• TITLE: Preparation of KOH/CaO/C Supported Biodiesel Catalyst and Application Process

  AUTHORS: Jianwei Zhang, Qingming Meng

  KEYWORDS: Solid base Catalyst, Biodiesel, Transesterification, Blending Impregnation

  JOURNAL NAME: World Journal of Engineering and Technology, Vol.2 No.3, August 4, 2014

  ABSTRACT: KOH/CaO/C supported catalyst was prepared via incipient wetness impregnation and used in synthesis of biodiesel. First, the effects of carrier/active components mass ratio, calcination temperature and calcination time on catalytic activity were investigated aiming at biodiesel yield, and the optimal process conditions for preparation of KOH/CaO/C catalysts were: mass ratio of C/CaO was 4:6; KOH solution (mass concentration) was 25%; impregnation time was 24 h; drying temperature was 105°C and time was 4 h; calcination temperature was 500°C and time was 5 h. Then the complex catalysts prepared under the optimal conditions were applied to synthesize biodiesel, and the effects of dose of catalyst, reaction temperature, and reaction time on the yield of biodiesel were investigated. At last, the optimal process conditions for synthesis of biodiesel were concluded: methanol-oil ratio was 10:1; catalyst dose was 2% of that of soybean oil; reaction temperature was 65°C; reaction time was 5 h. The yield of as-prepared biodiesel could be 98%.