Effect of Austempering Time on Microstructure and Wear Resistance of Ductile Iron Castings ()
Abstract
An experimental investigation was carried out to study the structure of ductile iron castings which were selected to perform the investigation: 1.4% Ni - 0.3 Mo and 2.4% Ni - 0.3 Mo. After austenitizing at 880℃ for 1.3 hr, the two alloys were austempered at 250An experimental investigation was carried out to study the structure of ductile iron castings which were selected to perform the investigation: 1.4% Ni - 0.3 Mo and 2.4% Ni - 0.3 Mo. After austenitizing at 880℃ for 1.3 hr, the two alloys were austempered at 250℃ and 350℃ for time intervals of 60, 120, 240 minutes. Microstructure observation and measurement of UTS, and adhesive wear resistances were reported as functions of austempering time. The results also showed that the obtained structure properties are not believed to be the best possible, but rather they should be viewed as what can be expected with reasonable controls. Production of a conventional spare gear from austempered ductile iron was aimed and concluded at a later stage. The same casting and treating conditions attributed to the optimum structure properties were used for production of the gear. and 350℃ for time intervals of 60, 120, 240 minutes. Microstructure observation and measurement of UTS, and adhesive wear resistances were reported as functions of austempering time. The results also showed that the obtained structure properties are not believed to be the best possible, but rather they should be viewed as what can be expected with reasonable controls. Production of a conventional spare gear from austempered ductile iron was aimed and concluded at a later stage. The same casting and treating conditions attributed to the optimum structure properties were used for production of the gear.
Share and Cite:
Rijab, M. and Al-Mosawi, A. (2014) Effect of Austempering Time on Microstructure and Wear Resistance of Ductile Iron Castings.
Open Access Library Journal,
1, 1-5. doi:
10.4236/oalib.1101032.
Conflicts of Interest
The authors declare no conflicts of interest.
References
[1]
|
Hughes, I.C.H. (1998) Ductile Iron. ASM Handbook: Casting, Vol. 15, ASM International, Materials Park, 647-666.
|
[2]
|
Massone, J.M., Boeri, R.E. and Sikora, J.A. (1996) Decomposition of High Carbon Austenite in ADI. AFS Transactions, 133-137.
|
[3]
|
Ductile Iron Society (2001) Ductile Iron Data for Design Engineers.
|
[4]
|
Eid, M.R. (2001) Effect of Graphite Nodularity on Structure and Mechanical Properties of Austempered Cast Iron. M.Sc. Thesis, Cairo University, Cairo.
|
[5]
|
Abd Elhakeem, A.A. (2002) Austempering of Spheroidal Graphite Cast Iron. M.Sc. Thesis, Cairo University, Cairo.
|
[6]
|
Forrest, R.D. (2000) Austempered Ductile Iron for Both Strength and Toughness Part II. Machine Design, 134-146.
|
[7]
|
Elliott, R. (2004) Austempering of an Mn-Mo-Cu Alloyed Ductile Iron Part 1—Austempering Kinetics and Processing Window Part II. Materials Science and Technology, 12, 233-248.
|
[8]
|
Gundlach (2006) Monitoring the Bainite Reaction during Austempering of Ductile Iron and High Silicon Cast Steel by Resistivity Measurement Part III. AFS Transactions, 32, 17-24.
|
[9]
|
Young, J.M. (2008) Influence of Austempering Temperature on the Characteristics of Austempered Ductile Iron Alloyed with Cu and Ni. AFS Transactions, 43, 113-122.
|
[10]
|
Morton, P.A. (2009) A Guide to Mechanical Properties Possible by Austempering 1.5% Ni - 0.3% Mo Ductile Iron Part II. AFS Transactions, 67, 78-93.
|
[11]
|
Seshan, S. (2010) Structure and Properties of ADI as Affected by Low Alloy Additions Part III. AFS Transactions, 56, 53-66.
|