The Bowing Parameters of Ca_{χ}Mg_{1-χ}O Ternary Alloys ()

Sinem Erden Gulebaglan^{1*}, Emel Kilit Dogan^{2}, Murat Aycibin^{2}, Mehmet Nurullah Secuk^{2}, Bahattin Erdinc^{2}, Harun Akkus^{2}

^{1}Department of Electric Program, Vacational School of Van, Yuzuncu Yil University, Van, Turkey.

^{2}Physics Department, Faculty of Sciences, Yüzüncü Yil University, Van, Turkey.

**DOI: **10.4236/jmp.2014.515155
PDF
HTML XML
4,140
Downloads
5,048
Views
Citations

On the basis of
first principles calculations using density functional theory, we explore the
structural and electronic properties of two binaries: CaO and MgO in rock salt
structures. Structural properties of the semiconductor Ca_{χ}Mg_{1-χ}O alloys are derived from total-energy minimization within the General Gradient
Approximation. The band gap bowing parameters dependence is very powerful
Calcium composition. The results offer that an average bowing parameter of Ca_{χ}Mg_{1-χ}O alloys is *b* = ~0.583$ eV. We analyzed
the volume deformation, charge transfer and structural relaxation effects of
the Ca_{χ}Mg_{1-χ}O alloys.

Share and Cite:

Gulebaglan, S. , Dogan, E. , Aycibin, M. , Secuk, M. , Erdinc, B. and Akkus, H. (2014) The Bowing Parameters of Ca_{χ}Mg_{1-χ}O Ternary Alloys. *Journal of Modern Physics*, **5**, 1546-1551. doi: 10.4236/jmp.2014.515155.

1. Introduction

Recently, the binary compounds such as TlAs, AlAs, ScN, GaN and their mixtures such as TlAlAs, ScGaN have been studied theoretically [1] -[3] , because the wide range of the band gap is important for microelectronics devices. Generally, monoxide compounds are known as rock salt structures (B1) at room temperature and under pressure. Y. Duan et al. [4] have been handled the electronic properties of XO (X = Be, Mg, Ca, Sr, Ba, Zn and Cd) for wrutzite, zincblende and rock salt structure. Ponce et al. [5] have analyzed theoreticaly and experimentaly electronic and optic properties of CaS nad CaO. Albuquerque and Vasconcelos [6] are reported structual, electronic and optical properties of CaO. Karki et al. [7] [8] have inversigated structual, dynamic and electronic properties of liquid MgO via density functional theory. Makaremi and Nourbakhsh have declerated structual, electronic and magnetic properties of Mgo nanolayers. Nishi et al. [9] have investigated experimentally metastable solid solutions film ZnO layers. Stolbov and Cohen [10] have studied the electronic structure for equilibrium MgO-CaO. Miloua et al. [11] have calculated the electronic properties of, theoretically. Besides, A. Srivastava et al. [12] calculated phase translations in alloys.

In this paper, we represent the bowing parameter of alloys by first principles density functional theory. To the best of our knowledge, no theoretical as well as experimental work has been performed thus far for the bowing parameter of. The aim of this paper is to understand the attitude of the bowing parameters and contribution to the gap bowing parameters. The paper is methodized as follows: computational methodology is given in Section 2. Results and discussion are represented in Section 3. The study is concluded in Section 4.

2. Computational Details

The calculations for CaO, MgO and in the rock salt structure were investigated within the generalized gradient approximation (GGA) of density functional theory (DFT) using the PWSCF code [13] . In Quantum Espresso, the examining is performed by utilizing the Kohn-Sham [14] formation established on the DFT. Total energies have been calculated by using ultrasoft pseudopotentials and plane-wave basis sets. The exchange- correlation potentials in the GGA [15] is separately used in the calculations. The electronic configurations used for the pseudo potentials were Ca(3p^{6}4s), Mg(2p^{6}3s) and O(2s^{2}2p^{4}). The Khon-Sham [14] orbitals were described using a plane wave basis set. The highest kinetic energy of a plane wave in the chosen fundamental set is known the cutoff energy. Specialize assignation of the cutoff energy is important for achieving accurate results with available computational process. The values of cutoff energies used in our calculations are summarized in Table 1.

The plane wave energy cut off is selected 90 Ry. Accurate Brillounin zone investigations are carried out using the standard special k-points technique of Monkhorst and Pack [16] . The Brillouin zone investigation was performed over a mesh points. Our calculations involve an 16 atom for alloys in a supercell. We start at MgO cluster and finish at CaO cluster.

3. Results and Discussion

3.1. Structural Properties of Binary Compounds

The ternary compounds are bordered by two binary compounds of CaO and MgO. In order to be able to analyze the energy band gaps and bowing parameters of ternary alloys, it is wholesome to study the CaO and MgO binary compounds in terms of their structural and electronic properties. By lessening the total energy with regards to the atomic positions and lattice parameters we carried out the structural optimization. Equilibrium lattice parameters are obtained by fitting the total energy with the different volumes according to the Birch equation of states.

The Birch equation of states [17] can be seen in the Equation (1):

(1)

where and are the bulk modulus and its pressure derivative at the equilibrium volume. The calcu-

Table 1. Ground state energies for equilibrium MgO and CaO with various cutoff energies.

lated values for the equilibrium of CaO and MgO are 4.805 Å and 4.263 Å, respectively. We represented and compered the equilibrium lattice parameter, bulk modulus and bulk modulus derivation in Table 2.

3.2. Structural Properties of

In this paper, we examined the effectiveness of the Vegard’s law for rocksalt alloys in its ground states. Ca composition dependent lattice constant of compounds is expressed as:

(2)

where, and are the lattice constants of the, CaO and MgO, respectively. The volve of the deflection from Vegard’s law can be calculated by Equation (2). The numerical calculations are fulfilled for the different situations. Seven compositions of alloys were checked: 0.125, 0.25, 0.375, 0.5, 0.625, 0.75 and 0.875. The calculated results of lattice parameters with respect to compositions are itemized in Table 3 from which we find that the lattice parameter increases with increasing Calcium composition because these results are due diognosis atomic radius. The atomic radius of Calcium and Magnesium are 194 and 145 picometers, respectively. We represented and compered the equilibrium lattice parameter of ternary alloys in Table 3.

The results also propose that the composition-dependent lattice parameter of the ternary alloys can be represented by a third-order polynomial equation,.

The bowing parameter, , is significant for investigating the band gap energy ternary alloys. The band gap energy of ternary alloys describe by the band gap energy of binary compounds, a quadratic interpolation of

Table 2. Itemized lattice parameter a, bulk modulus and bulk modulus derivation for the binary compounds MgO and CaO in rocksalt structure at equilibrium volume.

Table 3. Itemized lattice parameter a for the ternary alloys in rocksalt structure at equilibrium volume. All values are Å.

composition amount and the bowing parameter.

The band gap energy of ternary alloys given by

. (3)

Here, is the band gap energy of the ternary compound, is the band gap energy of the CaO compound, is the band gap energy of the MgO compound and is the band gap bowing parameter of. Bowing parameter is associated with the band gap energy. Figure 1 shows bowing parameter as a function of for ternary alloys. We calculated nearly linear variation for different composition, , determinating powerful. Our calculations show that according to the band gap energy of ternary alloys, bowing parameter decreases. The results are given by Table 4 and our results show that an average bowing parameter of is ~0.583 eV.

The combination-dependent bowing parameter function [21] was described as

(4)

The band gap of the ternary alloys are correlated with the band gaps of the binary compounds. The band gap bowing parameters have three physically contributions [17] .

Finally, the total band gap bowing parameter can be written by resolving into its components as:

. (5)

The effect of volume deformation causes the first term of bowing parameter, , in Equation (5). The no-

Figure 1. Composition dependence of the bowing parameter for ternary alloys.

Table 4. Itemized bowing parameter and contribution of the bowing parameter a for the ternary alloys in rocksalt structure at equilibrium volume.

tional response of MgO(CaO) to hydrostatical pressure states this term via the effect of the contribution of balanced lattice constant to the lattice constant of the alloy value.

(6)

A charge transfer in MgO and CaO at indicates the second term, , of the total band gap bowing parameter,

(7)

The third term, refers to the structural relaxation which takes place during the passing from the unrelaxed to the relaxed alloy

(8)

In Table 4, the values of bowing parameter, and its volume deformation component, charge exchange component and structural relaxation component are expressed for ternary alloys.

The results also propose that the combination-dependent bowing parameter of the alloys can be represented by a second-order polynomial equation, eV. The results clearly show that and are weak and composition dependent. The prime contribution to the gap bowing is from the. The interval of the calculated band gap bowing coefficient for alloys is from 2.900 to 4.234. One can note that for all contributions of the main addition to the gap bowing is owing to the effect. This could be correlated to the strong ionicity dissociable of the corresponding binary compounds (CaO and MgO). The contribution of the volume deformation term to the bowing parameter is gradually decreasing with concentration. Suddenly, in the case of the addition of the has increasing. The addition of the other structural relaxation is weak. Furthermore, and is nearly no effect to the bowing parameter. Namely, the is the only are component which enables the bowing parameter for alloys.

4. Conclusion

We have examined the electronic properties of the rocksalt ternary alloys as a function of Calcium composition by using the GGA method within DFT. The electronic band structures, which are calculated by using the lattice parameters composed from Vegard’s law. In the GGA, a band gap bowing parameters are achieved for rock salt ternary alloys. These results propose the physical condition of a composition dependent band gap energy for ternary alloys. Our calculations show that the ternary alloy’s the bowing parameters are very strong Calcium composition. The average bowing parameter is 0.583 eV for ternary alloys. The results clearly show that the is the only dominant component of the bowing parameter for alloys. Additionally and are weak.

Conflicts of Interest

The authors declare no conflicts of interest.

[1] | Erden Gulebaglan, S. (2012) Modern Physics Letters B, 26, 1250199-8. |

[2] |
Mazouza, H.M.A., Belabbesa, A., Zaouib, A. and Ferhat, M. (2010) Superlattices and Microstructures, 48, 560-568. http://dx.doi.org/10.1016/j.spmi.2010.09.012 |

[3] |
Moreno-Armenta, M.G., Mancera, L. and Takeuchi, N. (2003) Physica Status Solidi (B), 238, 127-135. http://dx.doi.org/10.1002/pssb.200301808 |

[4] |
Duan, Y., Qin, L., Tang, G. and Shi, L. (2008) European Physical Journal B, 66, 201-209. http://dx.doi.org/10.1140/epjb/e2008-00415-3 |

[5] |
Ponce, S., Bertrand, B., Smet, P.F., Poelman, D., Mikami, M. and Ganze, X. (2013) Optical Materials, 35, 1477-1480. http://dx.doi.org/10.1016/j.optmat.2013.03.001 |

[6] |
Albuquerque, E.L. and Vasconcelos, M.S. (2008) Journal of Physics: Conference Series, 042006, 1-4. http://dx.doi.org/10.1088/1742-6596/100/4/042006 |

[7] |
Karki Bijiya, B., Bhattarai, D. and Stixrude, L. (2006) Physical Review B, 73, 174208-1:7. http://dx.doi.org/10.1103/PhysRevB.73.174208 |

[8] |
Makaremi, N. and Nourbakhsh, Z. (2013) Journal of Superconductivity and Novel Magnetism, 26, 818-824. http://dx.doi.org/10.1007/s10948-012-1991-5 |

[9] |
Nishii, J., Ohtomo, A., Ikeda, M., Yamado, Y., Ohtani, K., Ohno, H. and Kawasahi, M. (2006) Applied Surface Science, 252, 2507-2511. http://dx.doi.org/10.1007/s10948-012-1991-5 |

[10] |
Stolbov, S.V. and Cohen, R.E. (2002) Physical Review B, 65, 092203-3. http://dx.doi.org/10.1103/PhysRevB.65.092203 |

[11] | Miloua, R., Miloua, F., Kebbab, Z. and Benramdane, N. (2008) ISJAEE, 6, 91-95. |

[12] |
Srivastava, A., Chauhan, M., Singh, R.K. and Padegaonker, R. (2011) Physica Status Solidi B, 248, 1901-1907. http://dx.doi.org/10.1002/pssb.201046508 |

[13] |
Baroni, S., Corso, A.D., de Gironcoli, S. and Giannozzi, P. http://www.pwscf.org |

[14] | Kohn, W. and Sham, L.J. (1965) Physical Review, 140, 1133-1138. http://dx.doi.org/10.1103/PhysRev.140.A1133 |

[15] |
Perdew, J.P., Burke, K. and Ernzerhof, M. (1996) Physical Review Letters, 77, 3865-3868. http://dx.doi.org/10.1103/PhysRevLett.77.3865 |

[16] |
Monkhorst, H.J. and Pack, J.D. (1976) Physical Review B, 13, 5188-5192. http://dx.doi.org/10.1103/PhysRevB.13.5188 |

[17] | Mehl, M.J., Klein, B.M. and Papaconstantopoulos, D.A. (1995) Intermetallic Compounds: Principles and Practice, Vol. 1: Principles. 195-210. |

[18] | Fei, Y. (1999) American Mineralogist, 84, 272-276. |

[19] | Karki, B.B., Stixrude, L., Clark, S.J., Warren, M.C., Ancland, G.J. and Crain, J. (1997) American Mineralogist, 82, 51-60. |

[20] |
Richet, P., Mao, H.K. and Bell, P.M. (1988) Journal of Geophysical Research: Solid Earth, 93, 15279-15288. http://dx.doi.org/10.1029/JB093iB12p15279 |

[21] | Drablia, S., Meradji, H., Ghemid, S., Labidi, S. and Bouhafs, B. (2009) Physica Scripta, 79, Article ID: 045002. |

Journals Menu

Contact us

+1 323-425-8868 | |

customer@scirp.org | |

+86 18163351462(WhatsApp) | |

1655362766 | |

Paper Publishing WeChat |

Copyright © 2024 by authors and Scientific Research Publishing Inc.

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.