Di(isothiocyanato)bis(4-methyl-4’-vinyl-2,2’-bipyridine) Ruthenium(II) Films Deposited on Titanium Oxide-Coated, Fluorine-Doped Tin Oxide for an Efficient Solar Cell ()
1. Introduction
Dye-sensitized solar cells (DSSCs) have been attracting abundant attention as technically and economically credible alternatives to traditional silicon-based solar cells [1-5]. As a key component of DSSCs, photosensitizers that can absorb sunlight and inject an electron into the conducting band of nanocrystalline TiO2 have been mainly focused in DSSC research; photosensitizers having a general structure of RuL2(X)2, where L stands for functionalized 2,2’-bipyridine such as 4,4’-dicarboxyl-2, 2’-bipyridine and X presents halide, cyanide, thiocyanate, thiolate, thienyl or ancillary water, have been extensively investigated over the past two decades [6-13]. Incident photon-to-current conversion efficiency (IPCE) is one of critical parameters for the evaluation of the performance of solar cells [14,15]. Among solar cells developed so far, that fabricated with N3 dye (cis-(dcbpy)2(NCS)2 ruthenium(II): dcbpy = 4,4’-dicarboxyl-2,2’-bipyridine) shows IPCE of about 85% in a visible light region [16].
Dyes are commonly immobilized onto a semiconductor (typically TiO2) surface with a functional group, such as carboxyl, phosphono or thio group in the dyes. Up to now, Ru(II) complexes without these functional groups cannot be candidates in DSSC research due to impossibility of immobilization; this drawback has limited the development of effective photosensitizers.
Herein, we report a new, electrochemically induced film formation method, which can immobilize di(isothiocyanato)bis(4-methyl-4’-vinyl-2,2’-bipyridine) ruthenium(II), and a novel type of dye-sensitized solar cells with sufficient IPCE.
2. Experimental Section
2.1. Instruments
1H NMR spectra were measured on a Bruker Ascend 400 spectrometer. Chemical shifts were determined with respect to the residual solvent peak (δ in ppm, J in Hz). Matrix-assisted laser desorption/ionization time-of-flight (MALDI-TOF) mass spectra were acquired on a Bruker autoflex speed-KE in a reflection mode with α-cyano- 4-hydroxycinnamic acid (CCA) as a matrix. FT-IR spectra were recorded on a JASCO FT/IR-610 spectrometer as KBr pellets. Ultraviolet-visible absorption (UV-vis)
spectra were measured on a Perkin Elmer Lambda 19 UV/vis/NIR spectrometer. Cyclic voltammograms were recorded on a CH instrument 701 electrochemical analyzer at a sweep rate of 100 mV·s−1 by using 0.1 M tetrabutylammonium perchlorate (TBAP) as an electrolyte solution, Pt wire as a counter electrode, and Ag/ AgCl as a reference electrode.
2.2. Materials
All reactions were performed under argon atmosphere. All reagents were purchased from Wako Pure Chemical Industries Ltd except for NH4SCN and sodium 4-vinylbenzenesulfonate, which were purchased from Nacac Tesque, Inc. The reagents were used as received, except for 4,4’-dimethylbipyridine which was recrystallized from methanol prior to use. Dry tetrahydrofuran (THF) was distilled over Na and benzophenone. 2-(4’-Methyl- (2,2’-bipyridin-4-yl)ethanol [17,18] and 4-methyl-4’- vinyl-2,2’-bipyridine [19] were synthesized according to the procedures in the literatures with some modifications. Di(isothiocyanato)-bis(4-methyl-4’-vinyl-2,2’-bipyridine)- ruthenium(II) was prepared by a method similar to that of bis(2,2’-bipyridine)diisothiocyanatoruthenium(II) [20].
2.2.1. 2-(4’-Methyl-2,2’-bipyridin-4-yl)ethanol
4,4’-Dimethyl-2,2’-bipyridine (6.8 g, 36.91 mmol) was dissolved in dry THF (400 mL), and the solution was cooled down to 0˚C by ice/water. Lithium diisopropylamide (20.3 mL, 2 M in THF, 40.60 mmol) was added dropwise to the solution. The purple solution was stirred at 0˚C for 2 h, and then a large excess amount of dry paraformaldehyde (5.5 g, 183 mmol as formaldehyde) was added all at once to the solution. The mixture was allowed to warm to room temperature and stir for 24 h. The color of the solution gradually turned from purple to light yellow. The reaction was quenched with distilled water (200 mL), and the solution was concentrated to about 50 mL under reduced pressure. The residue was extracted with dichloromethane (3 × 50 mL), and the extracts were concentrated under reduced pressure. The yellow viscous liquid remained was purified on neutral alumina gel column chromatography; after washing off unreacted 4,4’-dimethyl-2,2’-bipyridine with hexane/ethyl acetate (19:1, v/v), the yellow-colored fraction eluted with hexane/ethyl acetate (2:1, v/v) was collected. The fraction was condensed under reduced pressure to afford light-yellow oil (2.27 g, 29%). 1H NMR (400 MHz, CDCl3) δ (ppm): 8.56 (d, 1H, J = 5.0 Hz, PyH ), 8.50 (d, 1H, J = 5.0 Hz, PyH), 8.25 (s, 1H, PyH), 8.20 (s, 1H, PyH), 7.18 (dd, 1H, J1 = 5.0 Hz, J2 = 1.6 Hz, PyH ), 7.13 (d, 1H, J = 4.9 Hz, PyH), 3.96 (t, 2H, J = 6.5 Hz, CH2CH2OH), 2.95 (t, 2H, J = 6.4 Hz, CH2CH2OH), 2.44 (s, 3H, CH3).
2.2.2. 4-Methyl-4’-vinyl-2,2’-bipyridine (mvbpy)
2-(4’-Methyl-2,2’-bipyridin-4-yl)ethanol (2.27 g, 10.7 mmol), 4-t-butylpyrocatechol (0.1 g, 0.6 mmol) and finely powdered sodium hydroxide (4.28 g, 107 mmol) were successively added to benzene (5 mL). The blue mixture was then heated at 115˚C for 2 h under reduced pressure (<1 mmHg). The crude product was purified on silica gel column chromatography by using dichloromethane/methanol (100:1, v/v) as an eluent. The corresponding fractions were concentrated under reduced pressure to yield a colorless solid (1.0 g, 48%). 1H NMR (400 MHz, CDCl3) δ (ppm): 8.62 (d, 1H, J = 5.0 Hz, PyH), 8.55 (d, 1H, J = 5.0 Hz, PyH), 8.40 (s, 1H, PyH), 8.24 (s, 1H, PyH), 7.30 (dd, 1H, J1 = 5.1 Hz, J2 = 1.8 Hz, PyH), 7.14 (d, 1H, J = 4.9 Hz, PyH), 6.77 (dd, 1H, J1 = 14.32 Hz, J2 = 6.8 Hz, PyH), 6.09 (d, 1H, J =17.7 Hz, CH=CH2), 5.53 (d, 1H, J = 10.9 Hz, CH=CH2 ), 2.44 (s, 3H, CH3).
2.2.3. Di(isothiocyanato)bis(4-methyl-4’-vinyl-2, 2’-bipyridine) Ruthenium(II) [(NCS)2(mvbpy)2Ru(II)]
4-Methyl-4’-vinyl-2,2’-bipyridine (0.400 g, 2.04 mmol) was added to a solution of RuCl3 (0.211 g, 1.01 mmol) in DMF (20 mL). After the mixture was refluxed for 8 h in the dark, NH4NCS (6.367 g, 8.36 mmol) was added all at once at room temperature. The solution was refluxed again for 12 h and cooled down to room temperature. Upon adding methanol (200 mL) to the reaction mixture, a purple red powder was deposited, which was collected by filtration over a G4 glass filter. The purple powder was thoroughly washed with cold methanol (20 mL) and diethyl ether (15 mL), and dried for 12 h under reduced pressure to give (NCS)2(mvbpy)2Ru(II) (0.24 g, 38%). vmax (KBr, cm−1): 2104 (CN, s), 1400 (CH3, s). MALDITOF MS: calculated for C28H24N6S2Ru: [M]+ = 610.0548; found 610.0517 with isotope peaks in agreement with those obtained by a calculation.
2.3. Immobilization
The immobilization was performed in three steps under argon atmosphere. All solvents used were purged with argon for 15 min.
Step 1: The electrochemical treatment of an electrode was performed in a one-compartment cell according to the three-electrode method (TiO2-coated, fluorine-doped tin oxide (TiO2/FTO) as a working electrode, Pt wire as a counter electrode, and Ag/AgCl as a reference electrode) by using a CH instrument 701 electrochemical analyzer. These electrodes were dipped in an electrolytic solution containing 0.1 M of TBAP, and swept between 0-n-0 V (n = 2, 4, 6, 8, and 10) at a rate of 100 mV·s−1 with bubbling with argon during the electrolysis.
Step 2: After the electrolysis, the working electrode was soaked in a washing solvent for several seconds to remove adsorbents on the TiO2/FTO surface.
Step 3: The electrode was dipped into a solution of (NCS)2(mvbpy)2Ru(II) (1 mM) or the Ru complex/sodium 4-vinylbenzenesulfonate (1 mM and 1 mM, respectively) in DMF (30 mL), and kept for appropriate hours in the dark under argon atmosphere. Then, the electrode was taken out, washed with acetone (30 mL), and dried at room temperature in air to give the Ru complex film.
2.4. Measurement of Incident Photon-to-Current Conversion Efficiency (IPCE) of the Ru(II) Complex Films
A fluorometer (Horiba Jobin Yvon-Spex fluorolog, Horiba Inc.) equipped with a xenon lamp (Fluorolog instruments S.A., Inc.) was used in order to generate monochromatic lights from 350 nm to 750 nm with a width of 5 nm. The photon number was counted by an optometer (Photometer S370 UDT, Gamma Scientific Inc.). The electrical quantities were measured with an electrometer (Keithley 6514 system electrometer, Keithley Instruments Inc.). The DSSC was fabricated from TiO2/FTO coated with the Ru(II) complex film (photoanode), FTO (photocathode), and LiI/I2 (0.5 M/1.1 × 10−3 M) in CH3CN (mediator).
3. Results and Discussion
3.1. Formation of Di(isothiocyanato) bis(4-methyl-4’-vinyl-2,2’-bipyridine) Ruthenium(II) film on the Surface of a Titanium Oxide-Coated, Fluorine-Doped Tin Oxide Electrode
Because the present Ru(II) complex, di(isothiocyanato) bis(4-methyl-4’-vinyl-2,2’-bipyridine)ruthenium(II) [(NCS)2(mvbpy)2Ru(II)], has no functional group reactive with TiO2 such as carboxyl, phosphono or thio group, this complex cannot be immobilized onto the surface of TiO2-coated, fluorine-doped tin oxide (TiO2/ FTO) electrode with conventional film formation methods that have been adopted in the fabrication of DSSCs. Paying our attention to the fact that the Ru complex has vinyl groups, we at first tried to immobilize the Ru complex onto a TiO2/FTO surface by the electrolysis of a solution of the Ru complex. However, the attempt resulted in failure, most likely due to the decomposition of the Ru complex during the electrolysis. After numerous trials, we finally found a stepwise, electro-chemically induced film formation method to give a film-like deposit of the Ru complex on the surface of TiO2/FTO. This method is composed of three steps: Step 1, the electrolysis of a TiO2/FTO electrode only; Step 2, the washing of the electrode with a solvent; Step 3, the immobilization of the Ru complex upon immersing the washed electrode in a solution of the Ru complex. Figure 1 schematically represents the immobilization procedure.
The immobilization was found to be very sensitive to the history of the potential scanned onto a TiO2/FTO electrode (Step 1). Figures 2 and 3 show the cyclic voltammograms during the electrolysis of the electrodes in ranges of 0-n-0 V (n = 2, 4, 6, 8, and 10) at a rate of 100 mV·s−1 and the UV-vis spectra of the resultant electrodes. As shown in Figure 2, an irregular trace in the cyclic voltammograms was observed in a range of 1 - 3.5 V independent on the potential applied, which would correspond to irreversible oxidation.
Moreover, it is clear from Figure 3 that the electrochemically initiated film deposition of the Ru complex took place only when the electrode, potentially swept between 0-8-0 V at a rate of 100mV·s−1, was used. As shown in Figure 4, the electrode was colored after Step 3, undoubtedly indicating the film deposition. Moreover, the film deposited was insoluble in any solvents including aprotic polar solvents such as DMF and DMSO. These changes strongly support the deposition of the Ru complex through some reaction.
The electrochemically initiated film deposition method was also affected by solvents used in Steps 1-3. As shown in Figure 5, the solvent used in Step 1 influenced, to considerable extent, the quantity of the Ru
Figure 1. Schematic representation of the immobilization procedure.
Figure 2. Cyclic voltammograms of TiO2/FTO electrodes at a scan rate of 100 mV·s−1 in Step 1.
Figure 3. Uv-vis spectra of the resultant TiO2/FTO electrodes.
Figure 4. Electrodes before and after film deposition. (The electrodes were potentially swept between 0-8-0 V at a rate of 100 mV·s−1 in Step 1).
complex which finally immobilized on the surface of a TiO2/FTO electrode; although dichloromethane gave a better result than acetonitrile or methanol did, it was very hard to maintain steady conditions for the electrolysis due to the evaporation of dichloromethane upon bubbling argon during the electrolysis. Then, acetonitrile, which was better than methanol, was used in Step 1. In Step 2, no film was formed on the surface of TiO2/FTO, when the electrode was washed with DMF instead of acetonitrile. Because the Ru complex is soluble only in DMF and DMSO among common organic solvents, the immobilization, Step 3, was carried out by using DMF or DMSO. To our surprise, the film was just formed on a TiO2/FTO surface, only when DMF was used as the solvent.
Figure 6 shows the effect of the dipping time in Step 3 on the electrochemically initiated film deposition. The absorption arising from the Ru complex on the surface of TiO2/FTO increased continuously with prolonging the dipping time. In sharp contrast, when a TiO2/FTO electrode without any electrochemical treatment was directly dipped into a DMF solution of the Ru complex for 24 h, no absorption of the Ru complex was observed, indicating that the film was not formed at all on the TiO2/FTO surface without electrochemical treatment.