Characterization and Photoactivity of Cotton Loaded with ZnO NPs

Abstract

In this work, ZnO NPs were prepared by a simple co-precipitation technique. Cotton fibers loaded with ZnO NPs were prepared also. X-ray diffraction (XRD), scanning electron microscopy (SEM) and UV-Vis spectrophotometer have been used to characterize the prepared samples. The photocatalytic properties of the cotton loaded with ZnO (C-ZnO) and ZnO NPs, were studied under sunlight irradiation and lamp illumination as a function on time. The results showed that X-ray diffraction of ZnO NPs has a single-phase wurtzite structure with an average particle size of 29 nm. The morphology on the surface of ZnO NPs has a spherical shape. The optical band gap of ZnO nanoparticles was 3.37 eV. The photocatalytic confirms that C-ZnO exhibited higher photocatalytic activities than ZnO NPs.

Share and Cite:

Owis, A. , Elzayat, M. and Abdel-Baset, T. (2020) Characterization and Photoactivity of Cotton Loaded with ZnO NPs. Open Journal of Applied Sciences, 10, 111-117. doi: 10.4236/ojapps.2020.104009.

1. Introduction

ZnO oxide is an important n-type semiconductor material which receives a great interest for various applications due to its unique properties, such as a direct wide band gap (3.37 eV), large exciton binding energy (60 meV) at room temperature [1]. ZnO is one of the most photocatalyst due to low cost, nontoxic, high catalytic activity, thermal stability and environmental friendly [2] [3] [4]. ZnO has received much attention as a very promising photocatalyst for photocatalytic degradation of water pollutants, because it produces H2O2 more efficiently, it absorbs high efficiency with solar light and has higher rates of activities [5]. There are some routes used to improve the photocatalytic performance of ZnO, such as doping metal or non-metal ions likes Mg, C Al and graphite [6] [7] [8] [9], and combining ZnO with another semiconductor materials such as Tio2 [10] [11] [12]. It is very important to separate traditional catalysts from reaction systems. So we can use cotton fibers as supporting material. Cotton fibers have characterized by good moisture absorptivity, self-cleaning, high catalytic efficiency, low cost, easy recycling, and environmental sustainability [13]. In the present work, ZnO NPs are successfully synthesized by co-precipitation technique. The structural and optical properties of the ZnO NPs were investigated. Also, the photocatalytic activities of ZnO NPs and cotton loaded with ZnO for the degradation of MB under visible light and UV lamp were studied.

2. Experimental Work

2.1. Synthesis

Co-precipitation technique is suitable and a low-cost method for preparing ZnO NPs with a semispherical shape. ZnSO4 and NaOH solution were prepared separately and then mixed together. The solution was maintained at room temperature stirring for 2 h and heating of Zn(OH)2 at 70˚C for 24 h for drying. The dried ingots were heated at 400˚C for 4 h, after that time period, the powder was left to cool down slowly at room temperature to get pure ZnO.

The preparation of C-ZnO as follows, cotton fibers were washed several times with deionized water. Then clean it by acetone and ethanol, and let dried at room temperature for 24 h. Then the cotton fibers were immersed in the ZnO solution on stirrer for 1 h. The solution was filtrated, and dried the cotton fibers at 150˚C for 2 h. During this step, ZnO NPs were loaded on the cotton fiber.

2.2. Photocatalytic

The photocatalytic properties of ZnO NPs and C-ZnO were measured through the photo-degradation of MB dye under the direct sunlight and under the Philips 400 W lamp illumination. The experiments were carried out as follows: Solution of 10 ppm MB dye was prepared, then we have four beakers divided into two categories one for sunlight and the second for lamp illumination. Each beaker contains 100 ml of the dye. For each group, two photocatalytic were used for comparison, 0.1 g of ZnO nanoparticles and 0.4 gram of C-ZnO. UV-vis absorption was used to evaluate the photocatalytic degradation for MB dye.

2.3. Characterization Techniques

The obtained ZnO powder was characterized by X-ray diffraction (XRD), analysis of the samples was performed using a Rigaku miniflex diffractometer with CuKα radiation (λ = 1.5406 Å). Scanning electron microscopy (SEM; Inspect S, FEI, Holland) was used to determine the particle size and morphology of the prepared sample. Optical characterization was carried out using a Shimadzu UV-3600 UV-VIS-NIR spectrophotometer in the wavelength range 200 - 850 nm.

3. Results and Discussions

3.1. Characterization

XRD pattern of the pure ZnO exhibits a hexagonal wurtzite structure with a preferred (101) orientation as shown in Figure 1. The diffraction peaks corresponding to (100) and (002) planes of ZnO a hexagonal phase were also observed. Average crystalline size (D) is found to be ~29 nm by using Debye-Scherrer’s equation ( D = 0.94 λ / β cos θ ) [14] [15], where λ is wavelength of X-rays, β is full width at half maximum (FWHM) and θ is the diffraction angle.

The morphology of ZnO NPs, cotton fibers and C-ZnO were studied from SEM. Figure 2(a) shows the presence of ZnO sample in a spherical shape with average particle size ~29 nm. A smooth surface for the cotton fibers with no particles on its surface is shown in Figure 2(b), while C-ZnO is shown in Figure 2(c), its obvious differences, which were covered with a large quantity of ZnO NPs with a good dispersed. The stability of ZnO NPs on the surface of cotton fibers may be related to electrostatic bonding interactions between the negatively charged hydroxyl groups on cotton fiber and positively charged from the ZnO Nps.

The optical properties of the ZnO NPs were studied by UV-visible spectroscopy. The absorption spectra of ZnO NPs were shown in Figure 3. The sharp absorption edge is observed for the wavelength of about 376 nm in the absorption spectra which is characteristic of ZnO NPs. The optical band gap (Eg) for ZnO NPs was evaluated using the Tauc’s relation ( α h ν = B ( h ν E g ) 1 / 2 ) [16]

Figure 1. XRD diffraction patterns of ZnO.

Figure 2. SEM image of (a) ZnO NPs, (b) cotton fibers and (c) C-ZnO.

Figure 3. UV-Vis spectra of ZnO nanoparticles, and in the inset the bandgap calculation.

[17], where α is the absorption coefficient, B is a constant and hν is the photon energy. The optical band gap could be obtained by extrapolating the linear portion of the (αhν)2 versus hν plot to hν axis, as shown in the inset of Figure 3. The optical band gap was found to be 3.37 eV for the ZnO NPs, which is very close to the intrinsic band gap of ZnO.

3.2. Photocatalytic Activity

The percentage photocatalytic degradation was calculated by using the following equation:

Percent of degradation = [ ( C 0 C ) / C 0 ] × 100 = [ ( A 0 A ) / A 0 ] × 100

where, C0 represents the initial concentration of the dyes, C is the final concentration after illumination by UV light, A0 is the initial absorbance, and A is the variable absorbance [18].

In order to illustrate the potential application of ZnO NPs in wastewater treatment, we have investigated their photocatalytic activities for the degradation of MB under sunlight and 400 W UV lamp. Figures 4(a)-(d) show the absorbance spectra of the four systems at different degradation time. We show that with increasing degradation time, the intensity of the peaks decreases gradually, which indicates that MB is gradually photodegraded.

Under the UV-lamp irradiation for 2 h, the photocatalytic efficiencies of ZnO NPs and C-ZnO for MB are 62.2% and 73.8% respectively. In addition, the photocatalytic efficiencies of ZnO NPs and C-ZnO for MB under sunlight are 92.2% and 95.2% respectively. The results exhibit C-ZnO can provide high performance of photocatalytic activity for the degradation of MB than ZnO NPs. Also, the photocatalytic for the degradation of MB was very efficient in the presence of

Figure 4. ((a), (b)) ZnO NPs and C-ZnO under sunlight, ((c), (d)) ZnO NPs and C-ZnO under UV, respectively.

sunlight more than the UV lamp.

The mechanism of photocatalytic activity of C-ZnO as fellow: When the light energy is greater than or equal to the band gap energy, a high concentration of conduction band electrons (e) and valence band holes (h+) are created in the density of ZnO NPs attached on cotton. Positive hole (h+) interacts with hydroxyl group (–OH) on the cotton surface to produces hydroxyl radicals (•OH), which act as strong oxidants through the photocatalytic reaction. Moreover, photo generated electrons (e) react with an electron acceptor, such as O2 and are adsorbed on the surface of the catalyst or dissolved in water to produce superoxide radical anions O2• and •HO2. Free radicals react with each other, is major to formation of hydrogen peroxide and increasing gaseous oxygen in the photocatalytic reaction [19] [20] [21] [22]. All these react with methylene blue molecules for their full degradation.

4. Conclusion

Summarizing, we have prepared ZnO NPs and C-ZnO by a simple process co-precipitation method. ZnO NPs were characterized by XRD, SEM and UV-visible. SEM images showed that spherical like ZnO NPs of average diameter 29 nm were successfully prepared. ZnO NPs were loaded on the cotton in a homogeneous manner. ZnO NPs and C-ZnO were used as photocatalytics for the removal of methylene blue dye from aqueous solutions under sunlight and a philips 400 W lamp. The results showed that ZnO nanoparticles decomposed MB by 92.22% in the sunlight and 62.22% in the lamp illumination, and C-ZnO decomposes 95.27% of MB dye in the sunlight and 73.88% in the lamp illumination. In addition, C-ZnO was high performance of photocatalytic activity for the degradation of MB than ZnO NPs.

Conflicts of Interest

The authors declare no conflicts of interest regarding the publication of this paper.

References

[1] Cho, S., Jang, J.W., Lee, J.S. and Lee, K.H. (2012) Porous ZnO-ZnSe Nanocomposites for Visible Light Photocatalysis. Nanoscale, 4, 2066-2071.
https://doi.org/10.1039/c2nr11869f
[2] Pei, Z., Ding, L., Lu, M., Fan, Z., Weng, S., Hu, J. and Liu, P. (2014) Synergistic Effect in Polyaniline-Hybrid Defective ZnO with Enhanced Photocatalytic Activity and Stability. The Journal of Physical Chemistry C, 118, 9570-9577.
https://doi.org/10.1021/jp5020143
[3] Chu, F.H., Huang, C.W., Hsin, C.L., Wang, C.W., Yu, S.Y., Yeh, P.H. and Wu, W.W. (2012) Well-Aligned ZnO Nanowires with Excellent Field Emission and Photocatalytic Properties. Nanoscale, 4, 1471-1475.
https://doi.org/10.1039/C1NR10796H
[4] Lee, K.M., Lai, C.W., Ngai, K.S. and Juan, J.C. (2016) Recent Developments of Zinc Oxide Based Photocatalyst in Water Treatment Technology: A Review. Water Research, 88, 428-448.
https://doi.org/10.1016/j.watres.2015.09.045
[5] Vignesh, K., Suganthi, A., Rajarajan, M. and Sara, S.A. (2012) Photocatalytic Activity of AgI Sensitized ZnO Nanoparticles under Visible Light Irradiation. Powder Technology, 224, 331-337.
https://doi.org/10.1016/j.powtec.2012.03.015
[6] Qiu, X., Li, L., Zheng, J., Liu, J., Sun, X. and Li, G. (2008) Origin of the Enhanced Photocatalytic Activities of Semiconductors: A Case Study of ZnO Doped with Mg2+. The Journal of Physical Chemistry C, 112, 12242-12248.
https://doi.org/10.1021/jp803129e
[7] Wang, Y., Shi, R., Lin, J. and Zhu, Y. (2011) Enhancement of Photocurrent and Photocatalytic Activity of ZnO Hybridized with Graphite-Like C3N4. Energy & Environmental Science, 4, 2922-2929.
https://doi.org/10.1039/c0ee00825g
[8] Sun, W.J., Li, J., Mele, G., Zhang, Z.Q. and Zhang, F.X. (2013) Enhanced Photocatalytic Degradation of Rhodamine B by Surface Modification of ZnO with Copper (II) Porphyrin under Both UV-Vis and Visible Light Irradiation. Journal of Molecular Catalysis A: Chemical, 366, 84-91.
https://doi.org/10.1016/j.molcata.2012.09.010
[9] Lu, Y.H., Lin, W.H., Yang, C.Y., Chiu, Y.H., Pu, Y.C., Lee, M.H., Tseng, Y.C. and Hsu, Y.J. (2014) A Facile Green Antisolvent Approach to Cu2+-Doped ZnO Nanocrystals with Visible-Light-Responsive Photoactivities. Nanoscale, 6, 8796-8803.
https://doi.org/10.1039/C4NR01607F
[10] Upadhyay, G.K., Rajput, J.K., Pathak, T.K., Kumar, V. and Purohit, L.P. (2019) Synthesis of ZnO:TiO2 Nanocomposites for Photocatalyst Application in Visible Light. Vacuum, 160, 154-163.
https://doi.org/10.1016/j.vacuum.2018.11.026
[11] Yu, L., Chen, W., Li, D., Wang, J., Shao, Y., He, M., Wang, P. and Zheng, X. (2015) Inhibition of Photocorrosion and Photoactivity Enhancement for ZnO via Specific Hollow ZnO Core/ZnS Shell Structure. Applied Catalysis B: Environmental, 164, 453-461.
https://doi.org/10.1016/j.apcatb.2014.09.055
[12] Khodami, Z. and Ejhieh, A.N. (2015) Investigation of Photocatalytic Effect of ZnO-SnO2/Nano Clinoptilolite System in the Photodegradation of Aqueous Mixture of 4-Methylbenzoic Acid/2-Chloro-5-Nitrobenzoic Acid. Journal of Molecular Catalysis A: Chemical, 409, 59-68.
https://doi.org/10.1016/j.molcata.2015.08.013
[13] Fan, Y., Zhou, J., Zhang, J., Lou, Y., Huang, Z., Ye, Y., Jia, L. and Tang, B. (2018) Photocatalysis and Self-Cleaning from g-C3N4 Coated Cotton Fabrics under Sunlight Irradiation. Chemical Physics Letters, 699, 146-154.
https://doi.org/10.1016/j.cplett.2018.03.048
[14] Cullity, B.D. (1978) Elements of X-Ray Diffraction. 2nd Edition, Wesley Publishing Company, Inc., Reading.
[15] Samb-Joshi, K.M., Sethi, Y.A., Ambalkar, A.A., Sonawane, H.B., Rasale, S.P., Panmand, R.P., Patil, R., Kale, B.B. and Chaskar, M.G. (2019) Lignin-Mediated Biosynthesis of ZnO and TiO2 Nanocomposites for Enhanced Antimicrobial Activity. Journal of Composites Science, 3, 90.
https://doi.org/10.3390/jcs3030090
[16] Akbari, A., Mehrabian, M., Salimi, Z., Dalir, S. and Akbarpour, M. (2019) The Comparison of Antibacterial Activities of CsPbBr3 and ZnO Nanoparticles. International Nano Letters, 9, 349-353.
https://doi.org/10.1007/s40089-019-0280-8
[17] Abdel-Baset, T.A., Fang, Y.W., Duan, C.G. and Abdel-Hafiez, M. (2016) Magnetic Properties of Chromium-Doped ZnO. Journal of Superconductivity and Novel Magnetism, 29, 1937-1942.
https://doi.org/10.1007/s10948-016-3502-6
[18] An, D., Li, Y., Lian, X., Zou, Y. and Deng, G. (2014) Synthesis of Porous ZnO Structure for Gas Sensor and Photocatalytic Applications. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 447, 81-87.
https://doi.org/10.1016/j.colsurfa.2014.01.060
[19] Afzal, S., Daoud, W.A. and Langford, S.L. (2013) Photostable Self-Cleaning Cotton by a Copper(II) Porphyrin/TiO2 Visible-Light Photocatalytic System. ACS Applied Materials & Interfaces, 5, 4753-4759.
https://doi.org/10.1021/am400002k
[20] Zhang, L., Wan, J. and Hu, Z. (2017) Preparation and Photocatalytic Activity of TiO2-Wrapped Cotton Nanofiber Composite Catalysts. Bio Resources, 12, 6062-6081.
[21] Li, Y., Zhao, H. and Yang, M. (2017) TiO2 Nanoparticles Supported on PMMA Nanofibers for Photocatalytic Degradation of Methyl Orange. Journal of Colloid and Interface Science, 508, 500-507.
https://doi.org/10.1016/j.jcis.2017.08.076
[22] Casanova, L.C., Perez, A.A. and Rodenas, M.L. (2018) Effect of the Preparation Method (Sol-Gel or Hydrothermal) and Conditions on the TiO2 Properties and Activity for Propene Oxidation. Materials, 11, 2227.
https://doi.org/10.3390/ma11112227

Copyright © 2024 by authors and Scientific Research Publishing Inc.

Creative Commons License

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.