Effect of Curing Environment on the Strength Properties of Cement and Cement Extenders

DOI: 10.4236/msa.2015.61005   PDF   HTML   XML   4,729 Downloads   5,824 Views   Citations


Curing of cement based products such as concrete and mortar, is very important to achieve good strength and durable products. However the curing environment plays a pivotal role in the overall quality of cement based products in terms of strength development. ASTM C192 allows moist curing either in a fog room or under water. However, these must meet ASTM C511 which controls temperature, and specifically for water curing, the concentration of calcium ions in the curing solution. Unfortunately in many parts of the world, water curing literally means curing in tap water. This is done primarily because there is a lack of knowledge or ignorance regarding the mobility and roll of calcium hydroxide in the curing process. To illustrate the differences, in this study, straight ASTM Type I/II Portland cement and that mixed with powdered waste clay bricks as a cement extender were used to prepare two different batches of mortars. The chemical properties of the powdered waste clay brick met the ASTM C618 standard specifications for Class N pozzolans. Both mortar specimens were cured under two different environment comprising of either water and lime saturated water. Mortar specimens were tested for compressive strength at 3, 7, 14 and 28 days of either curing conditions. Test results indicated that mortar specimens cured in lime saturated water obtained higher strength than those cured in fresh water at all ages of curing. Statistical inference drawn from ANOVA testing showed that curing conditions had significant impact on strength development of the blended and unblended cement systems. The study recommends that testing of concrete and mortar samples and other research related works be performed in lime saturated water other than fresh water.

Share and Cite:

Bediako, M. , Kevern, J. and Amankwah, E. (2015) Effect of Curing Environment on the Strength Properties of Cement and Cement Extenders. Materials Sciences and Applications, 6, 33-39. doi: 10.4236/msa.2015.61005.

Conflicts of Interest

The authors declare no conflicts of interest.


[1] Sharp, J.H. (2006) Surely We Know All about Cement—Don’t We? Advances in Applied Ceramic, 105, 162-174.
[2] Global Cement Report (2014) International Cement Review.
[3] Vigil de la Villa, R., Fernandez, R., Rodr1guez, O., Garc1a, R., Villar-Cocina, E. and Fr1as, M. (2013) Evolution of the Pozzolanic Activity of a Thermally Treated Zeolite. Journal of Materials Science, 48, 3213-3224.
[4] Sabir, B.B., Wild, S. and Bai, J. (2001) Metakaolin and Calcined Clays as Pozzolans for Concrete: A Review. Cement and Concrete Composites, 23, 441-454.
[5] Tironi, A., Terezza, M.A., Scian, A.N. and Irassar, E.F. (2013) Assessment of Pozzolanic Activity of Different Calcined Clays. Cement & Concrete Composites, 37, 319-327.
[6] Agarwal, S.K. (2006) Pozzolanic Activity of Various Siliceous Materials. Cement and Concrete Research, 36, 1735-1739.
[7] Bediako, M., Gawu, S.K.Y. and Adjaottor, A.A. (2012) Suitability of Some Ghanaian Mineral Admixtures for Masonry Mortar Formulation. Construction and Building Materials, 29, 667-671.
[8] Samet, B., Mnif, T. and Chaaboni, M. (2007) Use of Kaolinitic Clay as a Pozzolanic Material for Cements: Formulation of Blended Cement. Cement and Concrete Composite, 29, 741-749.
[9] Toledo Filho, R.D., Gonclaves, J.P., Americano, B.B. and Fairbairn, E.M.R. (2007) Potential for Use of Crushed Waste Calcined Clay Brick as Supplementary Cementitious Material in Brazil. Cement and Concrete Research, 37, 1357-1365.
[10] Bediako, M. (2014) Laboratory Curing of Cement Based Products: The Perceptions of the Building Professionals. CSIR-BRRI Unpublished Technical Report.
[11] ASTM (2014) Standard Practice for Making and Curing Concrete Test Specimens in the Laboratory. C192-14, ASTM International, West Conshohocken.
[12] Irish Concrete Society (2004) The New Concrete Standards. Irish Concrete Society Publishers.
[13] Kosmatka, S.H. and Wilson, M.L. (2002) Design and Control of Concrete Mixtures. Portland Cement Association, Skokie.
[14] Mamlouk, M.S. and Zaniewski, J.P. (2006) Materials for Civil and Construction Engineers. Prentice Hall Publishers, Upper Saddle River.
[15] Bullard, J.W., Jennings, H.M., Livingston, R.A., Nonat, A., Scherer, G.W., Schweitzer, J.S., Scrivener, K.L. and Thomas, J.J. (2011) Mechanisms of Cement Hydration. Cement and Concrete Research, 41, 1208-1223.
[16] Neville, A.M. (1996) Properties of Concrete. 4th Edition, ELBS, United Kingdom.
[17] Ballester, P., Hidalgo, A., Mármol, I., Morales, J. and Sánchez, L. (2009) Effect of Brief Heat-Curing on Microstructure and Mechanical Properties in Fresh Cement Based Mortars. Cement and Concrete Research, 39, 573-579.
[18] Lothenbach, B., Winnefeld, F., Alder, C., Wieland, E. and Lunk, P. (2007) Effect of Temperature on the Pore Solution, Microstructure and Hydration Products of Portland Cement Pastes. Cement and Concrete Research, 37, 483-491.
[19] ASTM (2012) Standard Practice for Making and Curing Concrete Test Specimens in the Field. C31, ASTM International, West Conshohocken.
[20] Zemajtis, J.Z. (2014) Role of Concrete Curing. Portland Cement Association, Skokie.
[21] ASTM (2006) Standard Specification for Standard Sand. ASTM international, C778-13, West Conshohocken.
[22] ASTM (2012) Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolana for Use in Concrete. ASTM International, C618, West Conshohocken.
[23] ASTM (2007) Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (2-in or [50 mm] Cube Specimen). C109-03, ASTM International, West Conshohocken.
[24] ASTM (2007) Standard Test Method for Flow of Hydraulic Cement Mortar. ASTM International, C1437, West Conshohocken.
[25] Weng, T.L. and Cheng, A. (2013) Influence of Curing Environment on Concrete with Crystalline Admixture. Monatshefte für Chemie-Chemical Monthly, 145, 195-200.
[26] ASTM (2013) Standard Specification for Mixing Rooms, Moist Cabinets, Moist Rooms, and Water Storage Tanks Used in the Testing of Hydraulic Cements and Concretes. ASTM International, C511, West Conshohocken.

comments powered by Disqus

Copyright © 2020 by authors and Scientific Research Publishing Inc.

Creative Commons License

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.