Photoluminescence of Por-Si with High-ordered Mosaic Structure Received at Long Anodic Etching p-Si (100) in the Electrolyte with an Internal Current Source

HTML  Download Download as PDF (Size: 305KB)  PP. 217-221  
DOI: 10.4236/opj.2013.32B051    3,177 Downloads   4,511 Views  Citations

ABSTRACT

Photoluminescence spectra and nature of light-emitting centers of a porous silicon (por-Si) samples are given. The por- Si samples had high-ordered mosaic structure, which was received under long anodic etching p-Si(100) in electrolyte with an internal current source. The photoluminescence spectra were monitored at room temperature before and after annealing in air and vacuum. Comparative analysis of photoluminescence spectra of the por-Si samples annealed at different temperatures in air and vacuum shows that the thermal annealing conditions has significant effect on the intensity and spectral content of the photoluminescence spectra. The nature of the luminescence emission centers at different temperatures and annealing conditions was discussed.

Share and Cite:

K. B. Tynyshtykbaev, V. B. Glazman, M. A. Yeleuov, A. T. Isova, B. A. Rakymetov, D. Muratov and S. Z.Tokmoldin, "Photoluminescence of Por-Si with High-ordered Mosaic Structure Received at Long Anodic Etching p-Si (100) in the Electrolyte with an Internal Current Source," Optics and Photonics Journal, Vol. 3 No. 2B, 2013, pp. 217-221. doi: 10.4236/opj.2013.32B051.

Copyright © 2024 by authors and Scientific Research Publishing Inc.

Creative Commons License

This work and the related PDF file are licensed under a Creative Commons Attribution 4.0 International License.