An Evaluation of the Water Absorption and Density Properties of Expanded Polystyrene Sanded Concrete ()
1. Introduction
The continuous use of natural materials in construction especially in the production of concrete is having a devastating effect on bio-diversity and the ecosystem. It is because of the environmental consequences of the continuous exploitation of this natural resource that the professionals in the construction industries and built environment have always emphasized on the need to employ alternative materials in place of cement and aggregates. The idea of using alternative materials in replacing some of the natural materials in concrete production especially industrial agricultural and domestic wastes can continue to preserve our natural environment. The continuous exploitation of our natural environment in search of construction materials has adversely affected our environment such as pollution, and depletion of ozone layer through release of gases, etc.
The environmental impacts of the construction industry can be minimized through using waste and recycled materials to replace natural resources [1] .
In this research, expanded polystyrene (EPS) was introduced as a partial replacement of coarse aggregate to produce a lightweight concrete, which is expected to be economical, serviceable and meet the required standards for lightweight concretes. In this case, 30% by volume of natural coarse aggregate is replaced with EPS. Laboratory experiments were conducted on the qualities of concrete produced with this material as lightweight aggregate based on accepted standard codes of practice for concrete.
This work evaluated the mechanical properties in terms of density; and an evaluation of the absorption property using water absorption (capillary absorption and total immersion) as measures. Modeling of parameters using appropriate statistical/mathematical expressions was considered in order to predict and obtain necessary information for the appreciation of the use of this material.
This research work is limited to replacing only about 30% volume of natural coarse aggregate by equivalent volume of expanded polystyrene (EPS) to test for the density, and water absorption potentials. The essence of choosing 30% volume as replacement is to ease the control of the mix consistency and bonding because the more the volume of the polystyrene is, the more difficult the cohesion of the concrete ingredients especially with manual batching is.
Concrete is a widely used material the best in the construction industries, which made it to be very popular and versatile. Concrete is a composite inert material comprising of a binder course such as cement, mineral filler (body) or aggregates categorized as, fine (sand) and coarse (gravel or crush stone) aggregates and water [2] . Generally, concrete is classified as dense and lightweight. Lightweight concrete can be described as those weighing less than 1920 kg/m3. Lightweight concrete includes aerated, lightweight aggregates and non-fines concretes; while dense concrete is the popular types for reinforced concrete works with average density of about 2400 kg/m3 [3] . Concrete is a very variable material having wide range of strengths and stress-strain curves, it is any product or mass made by the use of cementing medium, and it is a composite material [4] . It is therefore possible to say that concrete comprise of mixing cement, aggregates, and often admixtures in appropriate proportions in the present of water; the mixture which undergo chemical reaction forming a paste, on allowed to cure become solid stone like substance. The compositions are natural materials usually extracted from the immediate environment. One of the most important properties of a good quality concrete is low water absorption [5] .
It is important to note that one of the transport mechanisms of water into concrete is through the action of capillary absorption and water which flow against gravity is transported spontaneously through the pores or voids of the concrete constituents.
Absorption is the process by which concrete takes in a liquid such as water or aqueous solution by capillary action; and the rate at which water enters the concrete is called absorptivity (or sorptivity) which depends on the size and interconnection of the capillary pores in concrete, and the moisture gradient existing from the surface [6] . Capillary water absorption of concrete is the phenomenon by which water is absorbed into concrete by capillary action and that the fineness of the capillary pores in concrete causes absorption of water by capillary action, as such, a measure of the rate of absorption provides a valuable image of the pore structure of concrete. Capillary action is a more suitable test on water penetration to express the quality of concrete for structures aboveground such as building [7] .
Density of concrete is one of the important parameters in structural behavior, and the density of concrete is a measure of its weight [8] . The higher the density of concrete the more is the dead load on structure. Most lightweight aggregate concrete used in structure, have equilibrium densities between 1760 - 1840 kg/m3 [9] . However, according to [10] [11] they have density range of 300 kg/m3 up to 1840 kg/m3, with dry density not exceeding 1840 kg/m3
Polystyrene is widely used as packaging materials in both large and medium industries and their post-consumer disposal/management post many problems. Expanded polystyrene is non-biodegradable thus constitute disposal problem, as such an environmental nuisance. Expanded polystyrene concrete has scope for nonstructural applications, like wall panels, partition walls, etc. [12] . Polystyrene wastes are becoming a major environmental concern due to the large quantities that are produced and the fact that they are not biodegradable. The development of concrete with non-conventional aggregates, such as polystyrene foam waste has been considered to improve the properties of the concrete, to lower costs, and to recycle polymeric materials [13] . Innovative technology utilizing industrial base waste is a way of modification and improvement in construction.
The use of high amount of EPS in concrete here means a high valuable waste disposal method, which provides solution for environmental problems and polymetric material is recycled. The high percentage of coarse aggregate replacement with EPS (i.e. 30%) means a high reduction in the dead load (self-weight) of the concrete elements, improvement of the properties of concrete and low costs, which translates to cheap and economic construction. This is an innovative technology using industrial based waste in a way of modification and improvement in construction.
2. Materials and Methods
2.1. Materials
The materials for this research experiments were locally sourced from the immediate environment in Kaura-Namoda, Zamfara state.
Dangote brand of ordinary Portland cement (OPC) of grade 42.5R conforming to BS and ASTM standards commonly used in concrete, free from hard lumps and of uniform colour with medium rate of hardening used as the binder was bought from local cement market in kaura Namoda.
The coarse aggregate (natural stone) was obtained from a nearby local aggregate site along Kaura Namoda/Zurmi local government in zamfara state. The maximum size of coarse aggregate for this experiment was 19 mm. The fine aggregate (sharp sand) was obtained from river Gagale in Kaura Namoda.
The Water used for the mixture and curing of concrete in the experiment is potable water from drinking water tap confirmed to be free from impurities/injurious amount of deleterious materials that can lead to concrete distress.
Expanded polystyrene (EPS) is obtained as waste from packaging container of workshops and laboratory equipment supplied to the Federal polytechnic, Kaura Namoda. The EPS was manually broken into approximately equal sizes of the natural coarse aggregate.
2.2. Batching and Mixing
The mix proportion which was obtained from the trail mix of water/cement ratio for the experiments was (1:2:4) by weight with a water/cement ratio of 0.5%. In this research, only 30% of the volume of the coarse aggregate was replaced by equivalent volume of EPS and mixing was manually done in the laboratory. The curing of concrete cubes was by total submerging inside water in a curing tank. The material mix proportion is as shown in Table 1.
3. Experimental Methods
3.1. Sieve Analysis
The sieve analysis for the aggregates was conducted to determine their particle size distribution using recommended standard sieve according to [14] . The fineness modulus of the fine and coarse aggregates as material proerties, were determined from the test as shown in Table 2.
3.2. Total Water Absorption
The experimental process is the same as that of capillary absorption except that; in this case, the cubes are totally submerged in water inside a container. The level of water above the face of concrete in the container is kept at nearly 50 mm. Increase in sample mass as water absorbed was measured by weighing each sample at prescribed time intervals of 1, 3, 5, 15, 30 min, 1, 4, 24, and 48, and the average of each set of two sample mass was computed as shown in Table 3.
Total mass of water absorbed at each time was obtained by subtracting the dry weight from the wet.
3.3. Capillary Water Absorption
Concrete specimens of 150 × 150 × 150 mm were casted from the mix. For the curing ages of 7 and 28 days, two specimens were produced and after 24 hours, they were demoulded and placed in water for curing under the same condition as those cubes for compression test until the required testing days.
The samples were, dried in an oven at 85˚C and at regular intervals removed and weighed to ensure constant dry weight before commencing the test and the maximum dry period was 72 hrs. The specimens were then, left to cool at normal room temperature in the laboratory before the water absorption test commenced. The capillary water absorption test was conducted by placing one face of each sample just in contact with water on supports in a shallow capillary tray and water was gradually added until the level rose above the contact surface by
Table 1. Concrete mix proportions for the experiment.
about (2 - 3) mm as depicted in Figure 1.
Increase in sample mass as water absorbed was measured by weighing each sample at prescribed time intervals of 1, 3, 5, 15, 30 min, 1, 4, 24, and 48, and the average of each set of two sample mass was computed as shown in Table 4. Total mass of water absorbed at each time, was obtained by subtracting the dry weight from the wet. The capillary water absorption was computed by the ratio of mass gained to the area of specimen in contact with water in (g/mm2) which was plotted against the square root of time, the initial slope of which was considered as water absorption coefficient. The area of concrete in contact with water is 150 mm × 150 mm = 22,500 mm2. Capillary water absorption coefficient is the slope of linear variation of absorbed water per unit area plotted against square root of time for the experiment.
3.4. Absorption Capacity (Moisture Content)
The absorption capacity is determined from the wet weight of cubes and their corresponding oven dry weights at specified period. If the initial wet weight is A, and the oven dried weight is B, the absorption capacity is then computed in percentage as;
All the water absorption tests were, conducted in accordance with [15] .
3.5. Density
Both the wet and dry densities of concrete cubes (150 × 150 × 150) size were performed.
Density,
(1)
Wet density,
Figure 1. Sample of capillary water test illustration.
(2)
Dry density,
(3)
The density test was conducted in accordance with [16] specifications.
4. Results and Discussion
The result of EPS concrete water absorption at 28 days of curing is presented in Table 5 and Figure 2 and Figure 3. These figures also showed that total water and capillary water absorption increases with time of suction. The modeled relationship between the capillary absorption and square root of time showed strong polynomial correlation with high regression value of 0.9997 (99.9%). While the modeled relationship between the capillary water gain and total water gain with time showed strong polynomial and logarithm relationship with regression value of 0.9556 (95.5%) and 0.9733 (97.33%) respectively. These from the graphs, shows that the high rate of water absorption at the early periods of the test has corresponding capillary coefficient of steep slope within the same period. The relationship between the variables Q the water absorption per unit area of the specimen and K the capillary coefficient, is that as the water absorption gets
Table 5. Capillary Water absorption after 28 days of curing.
higher, so does the capillary coefficient and the percentage of the variation is expressed by the correlation coeffient R2. Therefore, the values of R2 as depicted in the graphs shows a high percentage of variation.
Average initial wet weight of cubes A = 6041 g and average oven dry weight of cubes B = 5650 g.
The values for bulk and oven dry densities are computed using Equations (2) and (3) respectively and the results was found to be 1789 kg/m3 and 1674 kg/m3 for the bulk and oven dry density respectively. This is within the range for lightweight concrete as specified by [8] [9] . However, this result shows that the density of EPS modified concrete is less than the density of normal aggregate concrete.
5. Conclusion and Recommendations
5.1. Conclusions
The capillary absorption and square root of time showed a strong polynomial relationship with high regression while the capillary water gain and total water gain with time showed strong polynomial and logarithm relationship with high regression value.
The values for bulk density and dry density are found to be 1789 kg/m3 and 1674 kg/m3 respectively and this is within the acceptable range for lightweight concrete. The moisture absorption capacity of the EPS concrete was measured to be 6.9%.
5.2. Recommendations
It can be used to solve problems of weight, density, durability, and size structural elements. Further studies in this area will be of important to add more values to the use of this material in concrete production and waste management.