Effect of anneal temperature on electrical and optical properties of SnS:Ag thin films ()
Abstract
SnS and Ag films were deposited on glass sub-strates by vacuum thermal evaporation tech-nique successively, and then the films were annealed at different temperatures (0-300℃) in N2 atmosphere for 2h in order to obtain sil-ver-doped SnS ( SnS:Ag ) films. The phases of SnS:Ag films were analyzed by X-ray diffraction (XRD) system, which indicated that the films were polycrystalline SnS with orthogonal struc-ture, and the crystallites in the films were ex-clusively oriented along the(111)direction. With the increase of the annealing temperature, the carrier concentration and mobility of the films first rose and then dropped, whereas their re-sistivity and direct band gap Eg showed the contrary trend. At the annealing temperature of 260℃, the SnS:Ag films had the best properties: the direct bandgap was 1.3 eV, the carrier con-centration was up to 1.132 × 1017 cm-3, and the resistivity was about 3.1 Ωcm.
Share and Cite:
Jia, H. , Cheng, S. , Wu, X. and Yang, Y. (2010) Effect of anneal temperature on electrical and optical properties of SnS:Ag thin films.
Natural Science,
2, 197-200. doi:
10.4236/ns.2010.23030.
Conflicts of Interest
The authors declare no conflicts of interest.
References
[1]
|
El-Nahass, M.M., Zeyada, H.M., Aziz, M.S., et al. (2002) Optical properties of thermally evaporated SnS thin films [J]. Optical Materials, 20, 159-170.
|
[2]
|
Devika, M., Koteeswara Reddy, N., Sreekantha Reddy, D., et al. (2008) Synthesis and characterization of nanocrystal-line SnS films grown by thermal evaporation technique [J]. Journal of the Electrochemical Society, 155, 130-135.
|
[3]
|
Takeuchi, K., Ichimura, K.M., Arai, M.E., et al. (2003) SnS thin films fabricated by pulsed and normal electro chemical deposition [J]. Solar Energy Material and Solar Cells, 75, 427-432.
|
[4]
|
Muller R. S. (1991) Microsensor [M]. The Institute of Electrical and Electronics Engineers Inc, New York.
|
[5]
|
Albers, W., Hass, C., Vink, H.J., et al. (1961) Investi-gations on SnS [J]. Applied Physics, 32(10), 2220-2225.
|
[6]
|
Devika, M., Koteeswara, R.N., Ramesh, K., et al. (2006) Low resistive micrometer-thick SnS:Ag films for opto-electronic applications [J]. Journal of the Electrochemi-cal Society, 153,727-733.
|
[7]
|
Yakuphanoglu, F. (2009) Electrical conductivity, Seebeck coefficient and optical properties of SnO2 film deposited on ITO by dip coating [J]. Journal of Alloys and Com-pounds, 470, 55-59.
|