Non-Isothermal Degradation and Kinetics Studies of Some Quinaldine Azo Dye Complexes ()
1. Introduction
Azo compounds have been the subject of numerous spectral studies aimed at their identification or structural elucidation [1-4]. Interest in azo compounds stems from their ability to form metal chelates with metal ions [5,6]. The synthesis and characterization of new metal chelate derived from the kinaldine azo dye have been reported [7], but no report concerning the solid-state kinetics of such complexes has been published.
The aims of the present investigation are the preparation and elucidation of the geometrical structure of the metal chelates formed between divalent transition metal ions with different counter ions of acetate or chloride. The kinetics of the thermal decomposition of the azo dye complexes was also studied using dynamic thermogravimetric techniques.
2. Experimental
2.1. Material
All chemicals were used of pure grade (BDH or Aldrich). The preparation of the kinaldline azo dye followed the procedure described in the literature [7]. The chemical structure of this compound is shown in Figure 1.
2.2. Synthesis of Metal Chelates
The metal chelates were prepared by mixing equal volumes (40 ml) of hot ethanolic solutions of kinaladine azo dye and the metal salts (0.02 mol) Cu(OAc)2∙H2O, (Ni(OAc)∙2H2O or (NiCl2∙6H2O). The mixture left for 3 hours in steam bath, to adjust the pH to 6 - 8 by adding few drops of ammonia solution with continuous starring. The precipitate is washed with mixture of distilled water and ethanol until the filtrate becomes colorless; the chelates were collected and dried.
3. Results and Discussion
The stoichiometric ratio is (1:1) between the metal and ligand, the formulas of the three complexes under investtigation are [M LR mX. nH2O]∙yH2O, where M = Ni or Cu, X = OAc or Cl, m = 1, n = 3, y = 1, and LR represents 4-(R-phenylazo)-2-methyl quinoline derivatives, R = P-NH2 (L1) or R = p-COOH (L2) respectively. The calculated values of the suggested structural formula of the chelates are in good agreement with the values obtained from elemental analysis data (Table 1) dimethylsulfoxide was used as solvent at 25˚C to calculate the molar conductivities of the chelates which was found to be 13.25 - 20.2017 Ohm−1, these value are in non-electrolytic region which mean these chelates are of nonelectrolytic nature [8,9].
The water of hydration or coordination appear in the IR spectra of all metal chelates causes difficulty in drawing conclusions from the ν(OH) band for the hydroxyl groups of the free ligand, which would overlap those of water molecules. The participation of the hydroxyl group in the chelation is confirmed by the appearance of new band at 420 - 540 cm−1, which is related to νM-O vibrations [10]. The band at 370 - 400 cm−1 corresponds to ν (M-N) vibrations, [11] whereas the band at 340 - 350 cm−1 is attributed to ν(M-Cl) vibrations [12]. The bands at 1580 - 1420 cm−1 correspond to the ν(C=O) and ν(C-O) vibrations of CH3COO− [13], respectively.
Thermogravimetric Analysis
D Thermal analysis were performed on chelates of [CuL1(OOCCH3)(H2O)3]∙H2O (I); [NiL1Cl(H2O)3]∙H2O (II); and NiL2 (OOCCH3) (H2O)3]∙H2O (III). From TG curves weight loss at 120˚C is assigned to the loss of hydrate water. The coordinate water in the metal chelates is lost in the second step in the range 120˚C - 220˚C. For the complexes (I-III), the weight losses are approximately 3.15%, 4.03% and 3.57%, respectively, for the loss of a single water of hydration from the complexes. The weight losses of 11.96%, 12.17% and 10.74% for complexes (I-III), respectively, represent the removal of three coordinatively bounded water molecules from each of the complexes (I-III). From the TG curves in Figures 2 to 4, the remaining weight losses were 8.4%, 13.9% and 8.5% at a heating rate β = 15˚C/min; 13.9%, 15.5% and 11.0% at a heating rate β = 20˚C/min; and 16.5%, 17.5% and 13.5% at a heating rate β = 25˚C/min for complexes (I-III), respectively. These weight percentages are in good agreement with the values given in Table 1, for the complexes with the formulas suggested in Figure 5.
The TG results provide evidence for the formation of two types of oxides, depending on the heating rate. At aslow heating rate, the non-stoichiometric oxide of formula M1-xOx (0.1 £ x £ 0.5) formed, whereas the ideal oxide of suggested formula MO formed at the higher heating rate of 25˚C/min for all of the complexes.
The kinetics parameters, including the order of the decomposition (n), the activation energies (Ea), the frequency factors (Z) and the activation entropy (ΔS#), were calculated from the TG curves for runs performed in air in the temperature range of 200˚C - 600˚C using the Ozawa [14] and the Coats-Redfern methods [15]. The values of n, Ea, Z and ΔS# are given in Table 2. The mechanism involved in the decomposition is that of ran dom nucleation. The complexation of the quinolineazo dye derivatives with the transition-metal ions Ni(II) and Cu(II) in the presence of different counter-ions requires different amounts of energy, which may be due to the differences in the electronic configurations of the transition metals or to the existence of water molecules in the
Table 1. Elemental analysis, thermogravimetric analysis and molar conductance results for metals chelated with 4-(R-phenylazo)-2-methylquinoline derivatives.
Table 2. Thermal kinetics parameters and results of magnetic measurements of metals chelated with 4-(R-phenylazo) 2-methylquinoline derivatives.
Figure 1. The chemical structure of kinaldine azo dye.
(a)(b)(c)
Figure 2. (a) TG curves of 4-(R-phenylazo)-2-methylquinoline complexes (I); (b) Cats-Redfern method of analysis; (c) Ozawa method of analysis.
(a)(b)(c)
Figure 3. (a) TG curves of 4-(R-phenylazo)-2-methylquinoline complexes (II); (b) Cats-Redfern Method of analysis; (c) Ozawa method of analysis.
outer sphere, in addition to differences in several experimental factors. These factors may also influence the activation-energy values (Ea) that pertain to the thermal stability of the azo dye quinoline derivatives with Cu(II) and Ni(II) in the presence of different anions; these stabilities are arranged in the order II > III > I.
4. Conclusions
The Ni(II) and Cu(II) chelates of quinoline azo dye derivatived in the presence of different counter ions indicate octahedral arrangements which were obtained from the electronic spectral data and the magnetic moment values.
(a)(b)(c)
Figure 4. (a) TG curves o4-(R-phenylazo)-2-methylquinoline complexes (III); (b) Cats-Redfern method of analysis; (c) Ozawa method of analysis.
Figure 5. Suggested structural formulas of the Cu(II) and Ni(II) chelates.
The structures of the chelates have been determined and show that the monobasic bidentate ligand is coordinated to the metal ions through the OH and N as donor atoms in (1:1) (M:L) chelates. The kinetics parameters were calculated, and the higher values of Ea suggest a greater stability of the complexes. Furthermore, the negative values for the entropy of activation indicate that the activated complexes exhibit more ordered or more rigid structures.