Wang, F., Inoue, A., Han, Y., Zhu, S., Kong, F., Zanaeva, E., Liu, G., Shalaan, E., Al-Marzouki, F. and Obaid, A. (2017) Compounds, Soft Magnetic Fe-Co-Based Amorphous Alloys with Extremely High Saturation Magnetization Exceeding 1.9T and Low Coercivity of 2 A/m. Journal of Alloys and Compounds, 723, 376-384.
https://doi.org/10.1016/j.jallcom.2017.06.192

has been cited by the following article:

• TITLE: Influence of Phosphorus Content and Magnetic Annealing on Soft Magnetic Properties of Electrodeposited Amorphous FeMnP Alloy Films

  AUTHORS: Vincent Izerimana, Lei Ma, Huiliang Wu, Jianbo Wang, Qingfang Liu

  KEYWORDS: Phosphorus, Magnetic Annealing, Soft Magnetic Property, Natural Resonance Frequency

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.11 No.1, January 30, 2023

  ABSTRACT: In this work, we investigated the influence of phosphorus and magnetic anneal on the soft magnetic properties of electrodeposited FeMnP alloy films prepared by changing sodium hypophosphite concentrations. X-ray diffraction radiation patterns showed an amorphous structure of electrodeposited alloy films. The saturation magnetization and coercivity value decreased from 586 emu/cc to 346 emu/cc, and 52 Oe to 18 Oe, with the P content increased, respectively. The absorption resonance peak became broad as the P content increased, and the natural resonance frequency decreased from 1.8 GHz to 0.6 GHz, with the P content increasing. Magnetic annealing of samples reduced the magnetic damping, and natural resonance frequency increased by about 1.8 GHz and 3.5 GHz for the sample with lower and higher P content. The film structure with lower P content changed at 300˚C, while the structure remains unchanged for the films with higher P content. Thus, the crystallization temperature could depend on the P content in the film. FeMnP alloy films could be used in high-frequency devices.