Chen, D., Qu, Z., Shen, S., Li, X., Shi, Y., Wang, Y., Fu, Q. and Wu, J. (2011) Comparative Studies of Silver-Based Catalysts Supported on Different Supports for the Oxidation of Formaldehyde. Catalysis Today, 175, 338-345.
https://doi.org/10.1016/j.cattod.2011.03.059

has been cited by the following article:

• TITLE: Ag-Based Catalysts in Different Supports: Activity for Formaldehyde Oxidation

  AUTHORS: Rached Ousji, Zouhaier Ksibi, Abdelhamid Ghorbel, Céline Fontaine

  KEYWORDS: Formaldehyde Oxidation, TiO2, Al2O3, Silver (Ag), Impregnation, Sol-Gel

  JOURNAL NAME: Advances in Materials Physics and Chemistry, Vol.12 No.8, August 12, 2022

  ABSTRACT: Through the impregnation method, Ag catalysts with different support (such as TiO2 and γ-Al2O3) were prepared and then tested for catalytic oxidation of formaldehyde (HCHO) at low temperatures. The Ag/TiO2 catalyst exhibited strong catalytic performance, converting HCHO to CO2 and H2O at around 95°C. However, the Ag/Al2O3 catalysts showed much lower activity and reached100% conversion at 125°C. The Ag-based catalysts were next characterized by several methods (XRD, TEM, FT-R, BET and H2-TPR). Results of characterization revealed that support dramatically impactsthe size and dispersion of Ag particles. The XRD analysis showed the existence of different peaks of the silver on the surface of Al2O3 in the contrast with TiO2 no specific peaks exist. Therefore, the size of the Ag particles and their dispersion are the most important factors that affect their catalytic performance for formaldehyde oxidation. In terms of catalytic performance for HCHO oxidation, the Ag/TiO2catalyst possesses the best Ag dispersion, as well as the smallest Ag particle size.