He, M.R., Wang, S., Jin, K., Bei, H., Yasuda, K., Matsumura, S., Higashida, H.K. and Robertson, I.M. (2019) A Comparative Characterization of Defect Structure in NiCo and NiFe Equimolar Solid Solution Alloys under In Situ Electron Irradiation. Scripta Materialia, 166, 96-101.
https://doi.org/10.1016/j.scriptamat.2019.03.008

has been cited by the following article:

• TITLE: 2 GeV Electron Beam Irradiation Effects in Advanced Metallic Glasses

  AUTHORS: Monica Sorescu, Fatiha Benmokhtar, Douglas Higinbotham, Marcy Stutzman

  KEYWORDS: Metallic Glasses, Hyperfine Interactions, Magnetostriction, Radiation Effects, Mӧssbauer Spectroscopy

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.10 No.2, February 11, 2022

  ABSTRACT: Six amorphous alloys (Alloy 1: Fe56Co24Nb4B13Si2Cu1, Alloy 2: Fe68.5Co5Nb3Cu1Si15.5B7, Alloy 3: Fe75.3Ni0.8Cr0.9Si8.7B14.3, Alloy 4: Fe56Co24Cr10Nb4B3Si1Cu2, Alloy 5: Fe72.9Nb3Cu1Si16.2B6.9, Alloy 6: Fe83.3Si8.6Nb5.5B1.4Cu1.2) were selected in terms of their composition and magnetostriction constants and uniformly irradiated in a high radiation environment in Hall A of the Thomas Jefferson National Accelerator Facility. The 2 GeV electron beam irradiation-induced effects were characterized by Mӧssbauer spectroscopy. The microstructural changes were related to the evolution of the hyperfine magnetic field distributions and isomer shifts. In particular, the occurrence of stress centers in the amorphous materials was evidenced.