Wang, Y., Xiong, X., Li, G., Zhang, H., Chen, Z., Sun, W. and Zhao, X. (2012) Microstructure and Ablation Behavior of Hafnium Carbide Coating for Carbon/Carbon Composites. Surface and Coatings Technology, 206, 2825-2832.
https://doi.org/10.1016/j.surfcoat.2011.12.001

has been cited by the following article:

• TITLE: Double SiC Oxidation Protective Coating on C/C Composites Prepared by Spark Plasma Sintering

  AUTHORS: Xianghong Zhang, Changhu Yu, Lina Qiao, Beilong Zhao, Hao Huang, Hongxia Song, Xiaochen Sheng

  KEYWORDS: Carbon-Carbon Composites, Spark Plasma Sintering, Anti-Oxidation, Coating

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.5 No.6, November 22, 2017

  ABSTRACT: Easy oxidation of carbon limits applications of carbon-carbon composites in an oxygen-containing environment. In this study, a two-layer SiC coating was prepared on carbon-carbon composites by a Spark plasma sintering technology at 1350°C for 1 min. The coating was mainly composed of β-SiC and Si and well bonded with the substrate. The double SiC coating could effectively protect the C/C composites from oxidation at 1600°C for 120 h, and the corresponding weight loss was only 2.62%.