Kumar, S., Kumar, P. and Shan, H.S. (2008) Optimization of Tensile Properties of Evaporative Pattern Casting Process through Taguchi’s Method. Journal of Materials Processing Technology, 204, 59-69.
http://dx.doi.org/10.1016/j.jmatprotec.2007.10.075

has been cited by the following article:

• TITLE: Optimization of Process Parameter for Sawdust/Recycled Polyethylene Composites

  AUTHORS: Clement U. Atuanya, Chizoba M. Obele

  KEYWORDS: Okhuen Wood, Recycled Low Density Polyethylene, Taguchi Method, Tensile Properties

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.4 No.4, July 29, 2016

  ABSTRACT: In this paper, Okhuen wood sawdust and recycled polyethylene (RLDPE) were blended and then hot-pressed to produce sawdust/recycled polyethylene composite board. The optimum processing parameters for preparing the composite such as temperature, pressing time, sawdust/RLDPE content and pressure were investigated and optimized using L9 (34) Taguchi experimental design orthogonal array. The tensile strength of the various formulations was determined. The results show that those factors made different effects on the tensile strength of the composites. The optimized process conditions obtained are as follows: press time 7 min, press temperature 180°C, saw-dust/RLDPE 60:40%, press pressure 40kg/cm2. The average tensile strength of the optimized composite board was 13.991 MPa. The composite board met the standard for general purpose applications.