Mendes, A., Sanjayan, J.G., Gates, W.P. and Collins, F. (2012) The Influence of Water Absorption and Porosity on the Deterioration of Cement Paste and Concrete Exposed to Elevated Temperatures, as in a Fire Event. Cement and Concrete Composites, 34, 1067.

has been cited by the following article:

• TITLE: Effect of High Temperatures on the Microstructure of Cement Paste

  AUTHORS: M. A. Tantawy

  KEYWORDS: Cement paste, C-S-H, Portlandite, Dehydration, Microstructure

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.5 No.11, November 17, 2017

  ABSTRACT: The microstructural and compositional changes within the cement paste exposed to high temperatures were monitored by XRD, FTIR, TGA/DTA and SEM techniques to understand the nature of decomposition of C-S-H gel and the associated physicomechanical properties of thermally damaged cement paste. OPC paste (w/c ratio 0.27) was hydrated for 28 days then fired up to 750°C for 2 hours (heating rate 10°C/min). The relative mass percent of calcium hydrates and portlandite was estimated by calculations derived from TGA results. Beyond 450°C, the percentage of portlandite sharply diminishes and C-S-H progressively decomposes into C2S and C3S until complete loss of calcium hydrates content occurs at 750°C. An increase of the total porosity, severe loss in mechanical strength and propagation of harmful cracks occurs. The thermal shock as a result of cooling of the heated cement paste and the rehydration of lime enhance the propagation of harmful cracks.