1. Introduction
It is known that resistance to thermal- and air-thermal aggression and respectively to thermogradient of composite work-pieces made on ceramic matrix depends greatly not only on the value of the gradient at the mechanical stresses, which are mainly conditioned by the phases present in the material, thermal-processing regime and physical-chemical processes going on in the material during synthesis but also together with other factors, on their form [1] [2] [3] [4] .
If we take into consideration the fact that, when the nature of distribution of local mechanical stresses in solid bodies depends substantially on the form of a body, it is apparent that neglect of the form of a piece to thermogradient, will be associated with a big inaccuracy while determining the resistance of any specific work-piece [1] [2] . When we speak of the piece form, first of all, we have to imagine the curvilinear bodies with the surface of various curvature radii, which are mainly associated with the design of composite pieces. Composite materials are often characterized by rather complex profile relief, and in separate sections of its relief we often come across with very small radius curvature surfaces. It is namely pieces of such relief which are characterized by relatively high mechanical stresses, that is, static mechanical stresses [5] [6] [7] . When ceramic piece falls in the field of high thermal gradients the field efficiently acts on the section of a piece, in which mechanical stresses dominate, which is expressed in micro-efficiency, that is, in transformation of micro-cracks into macro-cracks and the final destruction of a piece [1] [2] [8] [9] [10] [11] . The fact is evident even without proving that in real conditions heat transmission is the last factor and temperature gradient between thermal emission and the piece at the border is bigger than the gradient formed in the piece, irrespective of the size of the piece.
2. The Main Part
As far as it is known for us, in technical literature available up to now impact of the form of any work-piece on the resistance of thermogradient of pieces has not been elucidated yet. The known Weibull’s formula [9] doesn’t consider certain definite complex forms of ceramic work-pieces and their effect not only on thermogradient of pieces, but also on their thermal resistance, at large. Likewise, a form of a piece is not considered in Bio’s [9] criterion, which characterizes value of temperature gradient between the piece surface and internal sphere. Fourier’s [7] formula offers us only coordinates of a spot to be considered. Kingery [8] in his computations for non-stationary regime, when piece surface temperature suffers abrupt alteration from T1 to T2, while average temperature of a body remains almost unchanged (that is we deal with thermal shock) and at the same time heat transition tends to infinity―uses the so-called form factor, but physical content is not explained by interpretations. Kingery often introduces the form factor in the formula for thermal resistance.
In most cases these are spherical, cylinder and infinitely flat plates, that is, simple forms. We considered necessary to define formula of thermogradient effect for relatively complex forms, that is, when the piece surfaces are intersections by various curvature radius angle. For determination of a piece resistance to thermal aggression the value of this angle has determining significance. Although we will repeat that in the complex material structure, the composition, texture and many factors have important impact on thermal resistance. Besides, we have to take into consideration that selection of adequate parameter for evaluation of methodology of thermal resistance and its assessment is rather difficult [12] . We think that determination of thermal resistance [13] only by means of the values of mechanical strength at stretching, E-elasticity module and temperature conductivity―a, are not sufficient. Special literature [14] - [19] offers formulas, which are used for evaluation of heat stability of work-pieces. Apparently in those relations alongside with mechanical strength, porosity and thermal stability, we have to consider quantitative evaluation of the above referred parameters. Limit of strength [6] at bending of porcelain material, when it causes its destruction, approximately equals to 56 MPa [20] . If we consider Budworth’s data [21] optimal volumetric quantity of pores in the matrix should not exceed 10%, and as a result, its mechanics suffers drastic worsening. At the same time Helga Gollisch-Szibov [22] offers optimal pore sizes―5 mcm. Kingery [8] offers insignificant porosity dependence on the factor of thermal resistance. According to the opinion of Strelov [23] at swift heating, porosity doesn’t affect significantly crack formation process.
It is known from practice [3] that increase of porosity in most cases contributes to the elevation of thermal stability, but due to the fact that at this moment mechanical properties are decreased, it is complicated to determine optimal porosity. On the basis of experiments carried out by us by Harcourt [24] method and water cooling at boiling regime, it was proved that work-pieces reveal maximum thermal resistance, when total closed porosity in the matrix is within 0.5% - 8%, and sizes of pores vary within 1 - 6 mcm. At the same time, they are more or less of spherical form and are spread equally in the matrix. [24] , that is, the material is consolidated. We tried to offer explanation for this problem and by the provision of a series of experimental data we formulated empirical formula, which establishes relations between urgent matrix parameters for ceramic materials and composites and coefficient of resistance to thermal gradient of the material (for ceramic materials and composites). Temperature gradient created in the work-piece which is placed in temperature field should be characterized by the effect. Between the bottom of the work-piece and the heat source, there occurs the temperature difference, or the primary gradient. At the same time, temperature field created along the piece height, is parallel to the initial field, and is perpendicular to the secondary one, or on the heat, created on the bottom of the work-piece. Thus, we received secondary temperature difference between heat source and the heat, created on the height of the work piece. Vector direction of both heat sources is on the same side. Thermogradient effect should be conditioned by emission trajectory curvature in temperature field and should be characterized by the coefficient, which shows durability of a piece in thermogradient conditions and speed of temperature equalization in the environment. It is measured in cm/sec.
r―is for the work-piece curvature radius for selected surface element, σbend is mechanics at bending, MPa; μ―Poisson coefficient; at―temperature conductivity; E―Young’s module; a―coefficient of linear expansion, dT/dy―thermal gradient for the selected y axis, along which thermogradient occurs, d1/2―half of piece wall thickness. It is necessary to allow some empiric assumptions, thus, e.g. that the piece from the side of heating should be flat, while the angle of joining of any two planes should be determined by curvature radius, which equals or exceeds
Spot of joining of two planes of a piece is computed according to the design, empirically, at 30% maximum angle. As to the thermal expansion and thermal stress, it is considered that expansion of the work-piece is free, that is, mechanically unlimited, while the stress can be formed not only due to abrupt alteration but also at gradual changes, since at one and the same thermal gradient and at various curvature radii, various stresses will be formed in the piece.
In our case, to test the formula we used the properties of celsian electro-ceramic piece synthesized in BaO-Al2O3-SiO2 system [25] and inserted the above listed properties in the formula by the succession of values given in the formula:
Thus, if we determine universal connection between mechanical and thermal properties of the material, and alongside with it, we’ll take into consideration the piece design and wall thickness, we’ll be able to compute resistance of a piece to thermal gradient.
3. Conclusion
The formula enables us to determine numerical value, which will conform to the resistance of the given work-piece to thermogradient. This latter is computed by the provision of numerical values of the characteristics of the main ceramic materials (composites) used in practice which are given in the formula [26] . Designers of ceramic pieces will be able to use the data, first of all, with the view of selection of thermogradient, if threshold value of thermal resistance of the given material is known.