The Potential of Silane Coated Calcium Carbonate on Mechanical Properties of Rigid PVC Composites for Pipe Manufacturing

Amin Al Robaidi, Ahmad Mousa, Sami Massadeh, Ibrahim Al Rawabdeh, Nabil Anagreh

.

DOI: 10.4236/msa.2011.25065                

Abstract

The inclusion of CaCO₃ and kaolin in polyvinyl chloride (PVC) polymer matrices greatly enhances the physical and mechanical properties of the composite. In this study, the effects of kaolin and surface treatment of CaCO₃ and kaolin particles on the microstructure and mechanical properties of PVC composites filled with kaolin particles via melt blending method were studied by means of SEM, tensile, Charpy impact testing, and FTIR. Treated and untreated kao-lin particles were dispersed in matrices of PVC resin at different concentrations up to 30 wt percentage. The tensile strength, elastic modulus, strain to failure and morphology of the resulting composites were measured for various filler loadings. Uniform dispersion of the fillers into the matrix proved to be a critical factor. SEM images revealed that small sized particles were more agglomerated than micron-sized particles and the amount of agglomerates increased with increasing particle content. Silane treated Kaolin-CaCO₃/PVC composites had superior tensile and impact strengths to untreated kaolin-CaCO₃/PVC composites. The Young’s modulus of all composites increased with increasing particle content up to maximum at 10% filler loading followed by gradually decreasing as content increased.

Keywords

Polyvinyl Chloride)/Calcium Carbonate (PVC/) Nano-Composite, Particle Size, Melt Blending, Tensile Testing, Charpy Impact

Conflicts of Interest

The authors declare no conflicts of interest.

References

[1]	G. A. Ari and I. Aydin, “Nanocomposites Prepared by Solution Blending: Microstructure and Mechanical Properties,” Journal of Macromolecular Science, Physics Part B, Vol. 47, No. 2, 2008, pp. 260-267.
[2]	S. Sun and C. Li, “Interfacial Structures and Mechanical Properties of PVC Composites Reinforced by CaCO3 with Different Particle Sizes and Surface Treatments,” Polymer International, Vol. 55, No. 2, 2006, pp. 158-164. doi:10.1002/pi.1932
[3]	R. Krishnamoorti and R. A. Vaia, “Polymer Nanocomposites,” Journal of Polymer Science Part B, Vol. 45, 2007, pp. 3252-3259. doi:10.1002/polb.21319
[4]	R. C. Advincula, “Encyclopedia of Polymer Science and Technology,” John Wiley & Sons, Hoboken, Vol. 11, 2004, pp. 114-134.
[5]	Y. Tsujii, K. Ohno, S. Yamamoto, A. Goto and T. Fukuda, “Structure and Properties of High-Density Polymer Brushes Prepared by Surface-Initiated Living Radical Polymerization,” Advances in Polymer Science, Vol. 197, 2006, pp. 1-45.
[6]	M. R. Buchmeiser, “Surface-Initiated Polymerization,” Advances in Polymer Science, Vol. 197, 2006, pp. 137-171.
[7]	B. Radhakrishnan and R. Ranjan, W. J. Brittain, “Surface Initiated Polymerizations from Silica Nanoparticles,” Soft Matter, Vol. 2, 2006, pp. 386-396. doi:10.1039/b516508c
[8]	A. Al-Irobaidi and N. A. Halim, “Correlation between Rheology; Processing and Microstructure in Polymers,” Dirasat, Vol. 27, No. 2, ?2000.
[9]	N. Khreische and A. Al-Irobaidi, “Micro Structure of Weathered Green House PE-Plastic Films,” Journal of Polymer Degradation and Stability, Vol. 32, 1991, pp. 105-114.